Industrial waste silica-alumina gel recycling: Low-temperature synthesis of mullite whiskers for mass production

Peiquan Chen,Xiaohua Gu,Siwen Liu,Shangwen Zhu,Tong Wang,Yanwei Zhu,Anyu Fan,Yan Liu

DOI: https://doi.org/10.1016/j.ceramint.2022.11.109

IF: 5.532

2023-02-12

Ceramics International

Abstract:The increasing demand for mullite whisker-reinforced, toughened ceramic materials and mullite raw materials that meet industrial requirements has prompted the search for new and alternative sources, as well as effective technologies to obtain the target products. In this work, mullite whiskers of high purity were synthesized by a vapor-liquid–solid (V-L-S) process using industrial waste silica-alumina gel and Al 2 (SO 4 ) 3 ·18H 2 O as raw materials, with AlF 3 ·3H 2 O and Na 2 SO 4 as additives. The effects of sintering temperatures on the mullitization reactions and mullite morphology were investigated by XRD, TG-DTA, SEM and so forth. The results suggest that the introduction of AlF 3 ·3H 2 O and Na 2 SO 4 alters the mullitization reaction path, which leads to an initial mullitization reaction temperature of 720 °C. The SEM results demonstrate that mullite whiskers transformed from secondary growth to anisotropic growth when the sintering temperature was increased from 720 °C to 825 °C. By analyzing the experimental results, the mechanism of AlF 3 ·3H 2 O-assisted growth of mullite whiskers with Na 2 SO 4 as the liquid phase template is proposed based on the "dissolution-precipitation" process. Herein, a novel and feasible solution for the recycling of silica-rich industrial waste is proposed, which offers new and simple insights into the high value-added recycling of industrial waste, which provides new ideas for the actual mass production of mullite whiskers.

materials science, ceramics