Abstract:Hydrous alumina powders, pure, seeded with alpha alumina, containing ammonium nitrate and containing both ammonium nitrate and seeds, were prepared by hydroxide precipitation. Their crystallization and sintering behaviour were investigated and mechanical properties of the ceramics were tested. Pure hydrous alumina transformed to alpha alumina crystals, with a size of ca. 200 nm, at 1200°C, after undergoing the usual metastable phase changes during heat-treatment. The powder needed to be sintered at 1600°C to achieve a high density. The ceramic had an average grain size of ca. 9 μm. Seeding lowered the transformation temperature to ca. 1120°C and caused the transformation to begin at ca. 600°C. The material could be sintered at 1500°C and had a grain size of 2 μm. The nitrate, predominantly present as ammonium nitrate, lowered the transformation temperature to ca. 1150°C and altered the proportion of the intermediate phases. However, the materials still had to be sintered at 1500°C to achieve >97% density. When both seed particles and nitrate ions were present the material almost completely transformed at 950°C to uniform crystals of alpha alumina with a size <60 nm that sintered to >99% theoretical density at 1450°C. The final ceramic had a uniformly grained (<1.0 μm) microstructure and exhibited strength up to 800 M Pa.

Preparation and research of fine-grained alumina with high mechanical properties

Plastic Deformation and Sintering of Alumina under High Pressure

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Preparation of fine-grained MoAlB with preferable mechanical properties and oxidation resistance

Preparation and Analysis of Mechanism of the High Fracture Toughness Alumina Ceramics with the Cheap Commercial Aluminum Hydroxide

Alumina-Based Ceramic Core Nano-Composites For Investment Casting

Fabrication of alumina ceramics with high flexural strength using stereolithography

High Toughness Alumina Ceramics with Elongated Grains Developed from Seeds

High fracture toughness alumina ceramic materials by elongated grains toughening from induced-seeds

Production of ultrafine alpha alumina powders and fabrication of fine grained strong ceramics

High fracture toughness alumina ceramic materials by elongated grains toughening from induced- seeds

Microstructure and Mechanical Properties of Porous Alumina Ceramics Fabricated by the Decomposition of Aluminum Hydroxide

Preparation and properties of porous alumina with highly ordered and unidirectional oriented pores by a self-organization process

Synthesis, Evaluation And Characterization Of Alumina Ceramics With Elongated Grains

Rheological Behaviours Of Slurries And Mechanical Properties Of Alumina With Additives

Preparation and Mechanical Property of Alumina Fibers Reinforced Thin Architectural Ceramic Plate

Hot-pressing of BeO Ceramics and Its Thermal Conductivity and Flexural Strength

Preparation of low-shrinkage and high-performance alumina ceramics via incorporation of pre-sintered alumina powder based on Isobam gelcasting

Al2O3 Ceramics with Well-Oriented and Hexagonally Ordered Pores: the Formation of Microstructures and the Control of Properties

Effect of MgO Content on the Microstructure and Properties of Zirconia-Toughened Alumina (ZTA) Ceramics by Hot Pressure Sintering10508-3010 M

Effect of trace alumina on mechanical, dielectric, and ablation properties of fused silica ceramics