Abstract:Al2O3-Cr2O3 refractories have excellent slag corrosion resistance and can adapt to the oxidation/reduction atmosphere in the smelting reduction ironmaking furnace. However, Al2O3-Cr2O3 refractories have poor mechanical properties and sintering properties. In order to improve the mechanical properties of Al2O3-Cr2O3 materials, the CaAl12O19 reinforced Al2O3-Cr2O3 composites were prepared by pressureless sintering process, and the influences of CaO content on the sintering properties, mechanical properties, and microstructure evolution of the composites were studied. The results show that a small amount of CaO can significantly improve the compactness of the composites, which is mainly due to the formed sheet-like CA6 fill the gap between the solid solutions, and reduces the porosity of the composites. In addition, the sheet-like CA6 makes the connection between solid solutions closer, and the intergranular fracture gradually transforms into a mixed mode of intergranular and transgranular fracture. The best mechanical propertie is observed at S4 with the CaO content of 2 wt.%. Compared with sample S0 without CaO, the hardness, compressive strength and flexural strength of the S4 were increased by 35.19 %, 49.69 %, and 68.34 %, respectively. The addition of excessive CaO will deteriorate the mechanical properties of the composites, because the formation of a large number of layered CA6 increases the porosity of the composites. Furthermore, a small amount of CaO addition can significantly improve the thermal shock resistance of the composites. After 10 and 20 thermal shock cycles, the strength loss rates of S4 are only 5.83 % and 8.74 %, respectively.

Rheological Behaviours Of Slurries And Mechanical Properties Of Alumina With Additives

The Influence of Rheology for Different Superplasticizer on High Alumina Low Cement Castable

Effects of Additives on Alumina Sheets Forming by A Novel Gel-Tape-Casting

Effects of glycerol addition on the slurry dispersion and mechanical properties of alumina ceramics prepared by gel-casting process

Dispersion and Gelation Properties of Alumina Systems with Isobam Assisted by Dicarboxylic Acids

Study on the Process of Si3N4 Ceramic with High Properties by Gel-casting

Influence of Particle Size and Aggregates on Translucent Alumina Ceramics Fabricated by Gelcasting

New gel-casting process for alumina ceramics based on gelation of alginate

Relation Between Rheological and Curing Behavior of Inorganic Foam Slurries in the Gel-Casting Process

Fabrication of alumina ceramics with high flexural strength using stereolithography

Effect of solid contents on the mechanical properties of SiC-10 wt.%AlN ceramic composites prepared by gelcasting

Gelcasting of Alumina with a Mixed PVP–MAM System

Rheological Behavior of Modified Starch-Alumina Oxide Suspensions

Preparation and Sintering Properties of Alumina Slurries with High Solid Loading

Microstructures and High-Temperature Strength of Gel-Casting Al2O3-based Ceramic Molds with Coated Aluminum Additive

Gelcasting of Alumina-Spinel Refractories

Gelcasting of Alumina Ceramic Components in Nontoxic Na-alginate–CaIO3–PVP Systems

Influence of Particle Size Distributions with Various Geometrical Standard Deviations on Slip-Cast Forming and Sintering Behavior in Submicron Alumina Powder Compacts

Microstructure and mechanical properties of CaAl12O19 reinforced Al2O3-Cr2O3 composites

Optimization of the Tape Casting Process for Development of High Performance Alumina Ceramics

Preparation and research of fine-grained alumina with high mechanical properties