Abstract:In the processing of porous ceramics, shrinkage from green body to sintered compact during drying and sintering is one of key concerns which affect microstructure and properties of the porous ceramics. Through releasing gases from the burning of the pore forming agents and volume expansion from formation of low density resultants during sintering, the sintering shrinkage can be effectively compensated and near net size preparation can be achieved. Herein, near net size porous alumina‐calcium aluminate ceramics with controllable shrinkage have been prepared by a combination of gelcasting and pore‐forming agent process through adjusting the amount of CaCO3 and polymethyl methacrylate (PMMA) microspheres added. Al2O3 and CaCO3 were used as raw material, polymethyl methacrylate (PMMA) microspheres were used as pore‐forming agent, isobutylene/maleic anhydride copolymer (Isobam104) was used as gelling agent and dispersing agent. The effects of the addition amounts of CaCO3 and PMMA in the slurry on the phase composition, shrinkage, porosity, and strength of porous alumina‐calcium aluminate ceramics were investigated. The results show that as the CaCO3 addition amount increases from 0 wt% to 20 wt%, the shrinkage of the samples gradually decreases from 7.3 % to ‐1.4 %, and the consequent porosity increases from 58 % to 66 %, while the compressive strength increases from 5.9 MPa to 15.5 MPa. When PMMA content increases from 10 wt% to 50 wt%, the shrinkage of the samples decreases first and then increases, the porosity increases from 51 % to 74 %, and the compressive strength decreases from 12.5 MPa to 5.3 MPa. The mechanisms for controlling of shrinkages during preparation of porous alumina‐calcium aluminate ceramics can be attributed to the following aspects: on one hand, gases release from burning of PMMA and decomposition of CaCO3 during sintering; on the other hand, volume expansion due to formation lower density calcium aluminates which come from the reactions between CaO and Al2O3. Near net size preparation technique is of great significance for the manufacture of porous ceramics since the subsequent machining cost can be effectively reduced.

Preparation of low-shrinkage and high-performance alumina ceramics via incorporation of pre-sintered alumina powder based on Isobam gelcasting

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

New gel-casting process for alumina ceramics based on gelation of alginate

Preparation of near net size porous alumina‐calcium aluminate ceramics by gelcasting‐pore‐forming agent processs

Dispersion and Gelation Properties of Alumina Systems with Isobam Assisted by Dicarboxylic Acids

Air permeable alumina-based porous ceramics with high performance prepared by novel gel casting route

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing

A novel composite binder design for direct ink writing alumina-based ceramics with enhanced strength at low sintering temperature

Fabrication of alumina ceramics with high flexural strength using stereolithography

Gelcasting of Alumina Ceramic Components in Nontoxic Na-alginate–CaIO3–PVP Systems

Preparation and properties of porous alumina with highly ordered and unidirectional oriented pores by a self-organization process

Ceramics with Ultra‐Low Density Fabricated by Gelcasting: an Unconventional View

Preparation And Properties Of High Strength Porous Si3n4 Ceramics

Gelcasting of Alumina with a Mixed PVP–MAM System

New approach to preparing near zero shrinkage alumina ceramic cores with excellent properties by vat photopolymerization

Preparation and research of fine-grained alumina with high mechanical properties

Preparation of Dense Mullite Ceramics through Gelcasting of Alumina Slurry Dispersed in Silica Sol

Ultrahigh‐strength Alumina Ceramic Foams Via Gelation of Foamed Boehmite Sol

Preparation of Porous Ceramic Materials by Alumina Fiber Framework

Gelcasting of alumina ceramics in the mixed acrylamide and polyacrylamide systems

Preparation of high performance dense Al 2 O 3 ceramics by digital light processing 3D printing technology