Preparation of high performance dense Al 2 O 3 ceramics by digital light processing 3D printing technology

Sijie Wei,Guifang Han,Xu Zhang,Jian Sun,Jingde Zhang,Weili Wang,Weibin Zhang,Lianhong Yang,Jianzhang Li

DOI: https://doi.org/10.1016/j.ceramint.2023.10.316

IF: 5.532

2023-12-04

Ceramics International

Abstract:The incorporation of a significant amount of organic materials in the fabrication process of Al 2 O 3 ceramics using digital light processing (DLP) 3D printing technology leads to a noticeable reduction in mechanical properties compared to those prepared using traditional methods. To enhance its mechanical performance of Al 2 O 3 ceramics, the addition of MgO and MgO-Y 2 O 3 sintering additives, along with a three-step curing method, has resulted in significant improvements. Al 2 O 3 ceramics fabricated with the addition of MgO exhibited a flexural strength of 454.2Ā MPa, Vickers hardness of 20.24Ā GPa and apparent porosity of 0.15Ā %. Similarly, the addition of MgO-Y 2 O 3 yielded Al 2 O 3 ceramics with a flexural strength of 491.6Ā MPa, Vickers hardness of 20.91Ā GPa, and apparent porosity of 0.11Ā %. These values exceed the typical flexural strength of Al 2 O 3 ceramics prepared using traditional methods. This research provides a fundamental basis for the production of high performance, dense, and complex shaped Al 2 O 3 ceramics using DLP 3D printing technology.

materials science, ceramics