Abstract:Digital light processing (DLP) is a promising additive manufacturing method for creating complex structural alumina ceramic with high precision, high efficiency, and low cost. However, printing large-size parts with high feature resolution by DLP, obtaining high-performance pastes, and optimizing the debinding process are challenges that still need to be overcome. In this study, an advanced top-down Matrix-DLP technology that seamlessly connects two high-definition-resolution DLP projectors, with high resolution and a large projection area, was used to achieve fine-structured large-size alumina green bodies. The homogeneous and stable non-self-levelling alumina pastes suitable for the DLP technology were developed, with a high solid loading up to 55 vol%, viscosity of 35.0 Pa s at 30 s−1, and good rheological properties by innovatively using 2.5 wt% P5318 as surface modifiers of alumina powders and with only a 0.244% volume of bubble residue by using 0.5 wt% BYK-066N defoamer in combination with a vacuum planetary stirring defoaming process. The debinding processes were designed based on TG-DSC analysis and then optimized, and it was proved that the segmented-atmosphere debinding process was the best approach and can obtain defect- and carbon residue-free bodies with uniform grain distribution, and can also achieve non-destructive debinding for the thick-walled parts with thickness greater than 10 mm. The effects of the debinding residual carbon and the solid loading on the microstructure and properties after sintering were also investigated. Consequently, the high-precision large-size alumina ceramic with good interlayer bonding, dense microstructure, and high microhardness of 17.92 GPa was obtained.

Polycrystalline alumina ceramic fabrication using digital stereolithographic light process

Influence of resin composition on rheology and polymerization kinetics of alumina ceramic suspensions for digital light processing (DLP) additive manufacturing

Fabrication and properties of alumina ceramics shaped by digital light processing as an additive manufacturing technology

Microstructures and mechanical properties of additively manufactured alumina ceramics with digital light processing

High‐Quality Translucent Alumina Ceramic Through Digital Light Processing Stereolithography Method

Preparation of high performance dense Al 2 O 3 ceramics by digital light processing 3D printing technology

Preparation of large-size alumina ceramic parts by DLP 3D printing using high-solid-loading paste and optimizing the debinding process

Fabrication and mechanical properties of triply period minimal surface porous alumina ceramics based on Digital Light Processing 3D printing technology

Study of alumina ceramic parts fabricated via DLP stereolithography using powders with different sizes and morphologies

Digital light processing‐based additive manufacturing of orientation‐controlled Al2O3 ceramics with improved damage tolerance

Dynamic mechanical properties of Alumina prepared by vat photopolymerization based on high solid loading slurry

Numerical Simulation of Sintering of DLP Printed Alumina Ceramics

Fabrication of alumina ceramics with high flexural strength using stereolithography

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Advancements in DLP 3D Printing: High Strength Alumina Toughened Zirconia Ceramics for Biomedical Applications

Microstructure refinement-homogenization and flexural strength improvement of Al2O3 ceramics fabricated by DLP-stereolithography integrated with chemical precipitation coating process

Rheological behavior and curing deformation of paste containing 85 wt% Al2O3 ceramic during SLA-3D printing

Fabrication of fine and complex lattice structure Al2O3 ceramic by digital light processing 3D printing technology

Additive manufacturing of Al2O3 ceramic core with applicable microstructure and mechanical properties via digital light processing of high solid loading slurry

Reinforcement effect in printing precision and sintering performance for liquid crystal display stereolithography additive manufacturing of alumina ceramics

Formation mechanism and controlling strategy of lamellar structure in 3D printed alumina ceramics by digital light processing