Abstract:This study highlights the importance of resin composition in ceramic stereolithographic 3D printing. Modulating the inclusion of a plasticizing agent and oligomer in the resin has significant effects on printed sample parameters such as cure depth and surface roughness. The choice of resin for ceramic stereolithographic 3D printing has a critical impact on printed ceramic preforms. In this study, we focused on the correlation between resin composition and parameters such as cure depth, surface morphology, lateral dimension, apparent layer height, and surface roughness. Special emphasis was placed on the addition of an oligomer and a plasticizing agent to a monomer‐based suspension. Four suspensions were studied: a 100% monomer (ethoxylated trimethylolpropane triacrylate) only suspension (M100), a suspension with 25% by weight plasticizing agent (polyethylene glycol) (PEG25), and two different suspensions with oligomer (urethane methacrylate) added at 25% (O25) and 50% (O50) by weight. Constant energy and printing parameters were used between suspensions. Adding a plasticizing agent (PEG25) was found to increase the cure depth and projected image of the samples, while additional oligomer with both amounts (O25 and O50) resulted in a decrease in the same parameters. The suspensions with oligomer were found to have increased surface roughness measured using the average deviation from the profile height mean line (Ra), with O25 at 13.47 μm and O50 at 11.47 μm. All suspensions had negative values of skewness (Rsk) in the range –0.4 to –1.2. PEG25 had the surface most distinct from a normally distributed surface with an Rsk of –1.12 and a kurtosis (Rku) value of 4.49. The use of the average length of a profile element (RSm) as a layer height estimation tool was explored and it was found that the RSm was within 10 μm of the printed layer height in all suspensions studied except for PEG25. This study highlights the importance of resin composition in ceramic stereolithographic 3D printing. Modulating the inclusion of a plasticizing agent and oligomer in the resin has significant effects on printed sample parameters such as cure depth and surface roughness.

Influence of resin composition on rheology and polymerization kinetics of alumina ceramic suspensions for digital light processing (DLP) additive manufacturing

Polycrystalline alumina ceramic fabrication using digital stereolithographic light process

Fabrication and properties of alumina ceramics shaped by digital light processing as an additive manufacturing technology

Microstructures and mechanical properties of additively manufactured alumina ceramics with digital light processing

Study of alumina ceramic parts fabricated via DLP stereolithography using powders with different sizes and morphologies

Digital light processing‐based additive manufacturing of orientation‐controlled Al2O3 ceramics with improved damage tolerance

Preparation of high performance dense Al 2 O 3 ceramics by digital light processing 3D printing technology

Relationship between the adhesion properties of UV-curable alumina suspensions and the functionalities and structures of UV-curable acrylate monomers for DLP-based ceramic stereolithography

Inter-particle interactions of alumina powders in UV-curable suspensions for DLP stereolithography and its effect on rheology, solid loading, and self-leveling behavior

Effects of debinding condition on microstructure and densification of alumina ceramics shaped with photopolymerization-based additive manufacturing technology

Rheological behavior and curing deformation of paste containing 85 wt% Al2O3 ceramic during SLA-3D printing

Influence of the Dispersants and Sintering Process on the Properties of Si2N2O Ceramics Via Digital Light Processing

High‐Quality Translucent Alumina Ceramic Through Digital Light Processing Stereolithography Method

Preparation of large-size alumina ceramic parts by DLP 3D printing using high-solid-loading paste and optimizing the debinding process

Numerical Simulation of Sintering of DLP Printed Alumina Ceramics

Additive manufacturing of Al2O3 ceramic core with applicable microstructure and mechanical properties via digital light processing of high solid loading slurry

Advancements in DLP 3D Printing: High Strength Alumina Toughened Zirconia Ceramics for Biomedical Applications

Microstructure refinement-homogenization and flexural strength improvement of Al2O3 ceramics fabricated by DLP-stereolithography integrated with chemical precipitation coating process

Enhancing Mechanical and Thermal Properties of 3D-Printed Samples Using Mica-Epoxy Acrylate Resin Composites—Via Digital Light Processing (DLP)

Fabrication and mechanical properties of triply period minimal surface porous alumina ceramics based on Digital Light Processing 3D printing technology

Effect of resin composition on cure depth, dimensional accuracy, and surface roughness in Al2O3 stereolithographic 3D printing