Enhancing Mechanical and Thermal Properties of 3D-Printed Samples Using Mica-Epoxy Acrylate Resin Composites—Via Digital Light Processing (DLP)

Velmurugan Senthooran,Zixiang Weng,Lixin Wu

DOI: https://doi.org/10.3390/polym16081148

IF: 5

2024-04-20

Polymers

Abstract:Digital light processing (DLP) techniques are widely employed in various engineering and design fields, particularly additive manufacturing. Acrylate resins utilized in DLP processes are well known for their versatility, which enables the production of defect-free 3D-printed products with excellent mechanical properties. This study aims to improve the mechanical and thermal properties of 3D-printed samples by incorporating mica as an inorganic filler at different concentrations (5%, 10%, and 15%) and optimizing the dispersion by adding a KH570 silane coupling agent. In this study, mica was introduced as a filler and combined with epoxy acrylate resin to fabricate a 3D-printed sample. Varying concentrations of mica (5%, 10%, and 15% w/w) were mixed with the epoxy acrylate resin at a concentration of 10%, demonstrating a tensile strength increase of 85% and a flexural strength increase of 132%. Additionally, thermal characteristics were analyzed using thermogravimetric analysis (TGA), and successful morphological investigations were conducted using scanning electron microscopy (SEM). Digital light-processing technology was selected for its printing accuracy and cost-effectiveness. The results encompass comprehensive studies of the mechanical, thermal, and morphological aspects that contribute to the advancement of additive manufacturing technology.

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to add mica as an inorganic filler to epoxy acrylate resin by using digital light processing (DLP) technology during 3D printing, in order to improve the mechanical and thermal properties of 3D - printed samples. Specifically, the researchers hope to achieve this goal through the following methods:

1. **Adding mica at different concentrations**: The researchers added 5%, 10% and 15% mica fillers respectively to explore the influence of different concentrations on the mechanical and thermal properties of 3D - printed samples.
2. **Optimizing dispersion**: In order to ensure the uniform dispersion of mica filler in the resin, the researchers added KH570 silane coupling agent.
3. **Comprehensive testing**: Through mechanical property tests (such as tensile strength and flexural strength), thermal analysis (such as thermogravimetric analysis TGA) and morphological analysis (such as scanning electron microscope SEM), comprehensively evaluate the performance of 3D - printed samples.

The main purpose of the research is to improve the mechanical strength and thermal stability of 3D - printed materials, thereby expanding their application range in the engineering and design fields. Through these improvements, the researchers hope to develop composite materials with higher performance, which are suitable for fields such as automobile parts, aerospace structures and advanced engineering materials.