Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Microstructure of low-temperature sintered AlN

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Migration of Liquid Phase and Grain Growth in Low-Temperature Sintering of AlN

Microstructure and thermal conductivity of aluminium nitride with (CaY)F3 as the sintering aid

Migration of Liquid Phases in Low-temperature Sintering of AlN

Effects of Li2o on the Low Temperature Sintering and Thermal Conductivity of Aln Ceramics

Microstructure and thermal conductivity of AlN ceramics with ultra-fine Y2O3 powder addition

EFFECT OF Li2O ON SINTERING OF AlN CERAMICS AT LOW TEMPERATURE

Low-Temperature Sintering of AlN Ceramics by Sm 2 O 3 -Y 2 O 3 -Cao Sintering Additives Formed Via Decomposition of Nitrate Solutions

Effect of Y2O3 on low temperature sintering and thermal conductivity of AlN ceramics

Characterization of the Microstructure of Sintered Aln by Sem and Tem

Microstructure and Thermal Conductivity of Spark Plasma Sintering AlN Ceramics

Effect Of Aln Content On The Pressureless Sintering Behaviors Of Sic-Aln Multiphase Ceramics

Structure and Properties of Aln Ceramics Prepared with Spark Plasma Sintering of Ultra-Fine Powders

Transient Liquid-Phase Sintering And Thermal Conductivity Of Ain

Thermal Conductivity of AlN Ceramics Sintered with CaF2 and YF3

Low temperature cofired and multilayer substrates

Microstructure and thermal conductivity of aluminium nitride with (YCa)F3 as sintering aid

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Improving thermal conductivity of aluminum nitride ceramics by refining microstructure

Toughening effect and mechanisms of AlN whiskers on a low‐temperature sintered AlNw/AlN ceramics