Abstract:A new type of non-oxide sintering additive of YH2 was introduced for the fabrication of AlN ceramics with high thermal conductivity and flexural strength. The effects of YH2 addition (0–5 wt%) on the phase composition, densification, microstructure, thermal conductivity and flexural strength of pressureless sintered AlN ceramics were investigated and compared with those Y2O3-added samples (1–5 wt%). The addition of 1 wt% YH2 led to an in-situ reduction reaction with oxygen impurities, the formation of Y2O3 and finally the formation of yttrium aluminate, which in turn improved densification and microstructure. A high flexural strength (408.69 ± 28.23 MPa) was achieved. The addition of 3 wt% YH2 increased the average grain size and purified the lattice. All these effects are believed to help achieve a high thermal conductivity of 184.82 ± 1.75 W·m−1·K−1. Although the thermal conductivity was close to the value of 3 wt% Y2O3-added sample, its strength was much increased to 381.53 ± 43.41 MPa. Meanwhile, it demonstrated a good combination of the thermal conductivity and flexural strength than the values reported in some literature. However, further increasing the YH2 addition to 5 wt% resulted in a high N/O ratio that inhibited the densification behavior of AlN ceramics. The current study showed that AlN ceramics with excellent thermal and mechanical properties could be obtained by the introduction of a suitable YH2 additive.

Low-Temperature Sintering of AlN Ceramics by Sm 2 O 3 -Y 2 O 3 -Cao Sintering Additives Formed Via Decomposition of Nitrate Solutions

Effect of Y2O3 on low temperature sintering and thermal conductivity of AlN ceramics

Effects of Y2O3 and Yttrium Aluminates As Sintering Additives on the Thermal Conductivity of AlN Ceramic Substrates

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Thermal Conductivity of AlN Ceramics Sintered with CaF2 and YF3

Microstructure of low-temperature sintered AlN

High Thermal Conductivity Silicon Nitride Ceramics Prepared By Pressureless Sintering With Ternary Sintering Additives

Phase composition, microstructure, electrical and thermal properties of TiN and Yb2O3-Sm2O3 doped AlN ceramics

Microstructure and thermal conductivity of aluminium nitride with (CaY)F3 as the sintering aid

Effects of YH2 addition on pressureless sintered AlN ceramics

Effects of Li2o on the Low Temperature Sintering and Thermal Conductivity of Aln Ceramics

Effect of Additive Sm2O3 on Synthesizing AlN Ceramics at High Pressure

Thermal Conductivity of AlN Ceramics with CaF2-YF3 Addition

EFFECT OF Li2O ON SINTERING OF AlN CERAMICS AT LOW TEMPERATURE

Synthesis of MgO-CaO-Al 2 O 3 -Sio 2 Nanocomposite Powder by Polymeric Complex Method As a Novel Sintering Additive of AlN Ceramics

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Microstructure and thermal conductivity of aluminium nitride with (YCa)F3 as sintering aid

Effect of Post-Sintering Heat-Treatment on Thermal Conductivity of Si3N4 Ceramics Containing Different Additives

Microstructure and thermal conductivity of AlN ceramics with ultra-fine Y2O3 powder addition

Effect of CeO2, Dy2O3, Yb 2O3 and y2O3 additives on thermal conductivity of silicon nitride ceramics