Abstract:A new type of non-oxide sintering additive of YH2 was introduced for the fabrication of AlN ceramics with high thermal conductivity and flexural strength. The effects of YH2 addition (0–5 wt%) on the phase composition, densification, microstructure, thermal conductivity and flexural strength of pressureless sintered AlN ceramics were investigated and compared with those Y2O3-added samples (1–5 wt%). The addition of 1 wt% YH2 led to an in-situ reduction reaction with oxygen impurities, the formation of Y2O3 and finally the formation of yttrium aluminate, which in turn improved densification and microstructure. A high flexural strength (408.69 ± 28.23 MPa) was achieved. The addition of 3 wt% YH2 increased the average grain size and purified the lattice. All these effects are believed to help achieve a high thermal conductivity of 184.82 ± 1.75 W·m−1·K−1. Although the thermal conductivity was close to the value of 3 wt% Y2O3-added sample, its strength was much increased to 381.53 ± 43.41 MPa. Meanwhile, it demonstrated a good combination of the thermal conductivity and flexural strength than the values reported in some literature. However, further increasing the YH2 addition to 5 wt% resulted in a high N/O ratio that inhibited the densification behavior of AlN ceramics. The current study showed that AlN ceramics with excellent thermal and mechanical properties could be obtained by the introduction of a suitable YH2 additive.

Effect of Additive Sm2O3 on Synthesizing AlN Ceramics at High Pressure

Effect of Additive Sm2O3 on Synthesizing AlN Ceramics at High Pressure

RESEARCH ON THE REACTION SYNTHESIS OF AlN-BASED CERAMICS WITH THE ADDITION OF Y2O3

Effects of YH2 addition on pressureless sintered AlN ceramics

Effect Of Aln Content On The Pressureless Sintering Behaviors Of Sic-Aln Multiphase Ceramics

Low-Temperature Sintering of AlN Ceramics by Sm 2 O 3 -Y 2 O 3 -Cao Sintering Additives Formed Via Decomposition of Nitrate Solutions

Phase composition, microstructure, electrical and thermal properties of TiN and Yb2O3-Sm2O3 doped AlN ceramics

Effect of impregnating and heat treatment on microstructure and properties of pressureless sintering AlN/h-BN composite ceramics

Structure and Properties of Aln Ceramics Prepared with Spark Plasma Sintering of Ultra-Fine Powders

Effect of Y2O3 on low temperature sintering and thermal conductivity of AlN ceramics

Effects of Y2O3 and Yttrium Aluminates As Sintering Additives on the Thermal Conductivity of AlN Ceramic Substrates

Effect of AlN and ZrO2 on the Microstructure and Property of the 2Si-B-3c-n Ceramic

Effect of composite sintering aids system on properties of pressureless sintered AlN ceramics

Effect of Carbon on Properties of Pressureless Sintered AlN Ceramics

Raction synthesis of Y2O3/A1N ceramic and mechanism of densification

Si<sub>3</sub>N<sub>4</sub>/BN Composite Ceramics with Nd<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-Y<sub>2</sub>O<sub>3</sub> Ternary Additives by Pressureless Sintering

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Effect of Al 2 O 3 addition on properties of non-sintered SiC–Si 3 N 4 composite refractory materials

Fabrication and Properties of Pressureless Sintered Si<sub>3</sub>N<sub>4</sub>/BN Composite Ceramics with La<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-Y<sub>2</sub>O<sub>3</sub> as Sintering Additives

Electrical properties of SiC-AlN ceramics pressureless sintered under N2 atmosphere

Pressureless Sintering and Properties Investigation of Silicon Nitride