Abstract:SiC-4 vol% BN composites were hot-pressed at 2050°C for 4 h at 40 MPa in a N2 atmosphere using micron-sized β-SiC and h-BN starting powders with 1 vol% sintering additives. Four batches were prepared using four different types of additive systems, i.e. Y2O3-Sc2O3, Yb2O3-CaO, Yb2O3-MgO, and Al2O3-AlN-Y2O3. The electrical, thermal, and mechanical properties of the SiC-4 vol% BN composites, which are primarily limited by the intrinsic weakness of h-BN and by the point defects (BC and AlSi) created by the dissolution of B and Al in the SiC lattice, were successfully tuned with the use of different additive systems. The electrical conductivity of SiC-4 vol% BN composites improved ~fivefold, i.e. from 2.6 (Ω·cm)−1 for the Al2O3-AlN-Y2O3-containing specimen to 13.9 (Ω·cm)−1 for the Y2O3-Sc2O3-containing specimen, owing to grain-growth-assisted N-doping and the elimination of Al-derived acceptors. Thermal conductivity was altered by 16% with the use of different additive systems. Fracture toughness dramatically increased from 4.3 MPa∙m1/2 in Yb2O3-CaO-containing specimens to 7.3 MPa∙m1/2 in Y2O3-Sc2O3-containing specimens. The electrical conductivity, thermal conductivity, flexural strength, and fracture toughness of SiC-4 vol% BN composite sintered with 1 vol% Y2O3-Sc2O3 were 13.9 (Ω·cm)−1, 82.0 W·m−1 K−1, 505 MPa, and 7.3 MPa∙m1/2, respectively.

Si<sub>3</sub>N<sub>4</sub>/BN Composite Ceramics with Nd<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-Y<sub>2</sub>O<sub>3</sub> Ternary Additives by Pressureless Sintering

Fabrication and Properties of Pressureless Sintered Si<sub>3</sub>N<sub>4</sub>/BN Composite Ceramics with La<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-Y<sub>2</sub>O<sub>3</sub> as Sintering Additives

Fabrication and Properties of Pressureless Sintered Si<sub>3</sub>N<sub>4</sub>/BN Composite Ceramics with La<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-Y<sub>2</sub>O<sub>3</sub> as Sintering Additives

Fabrication and properties of Si3N4/BN composite ceramics by pressureless sintering with Yb2O3-Al 2O3-Y2O3 as sintering additives

Fabrication and Properties of Pressureless Sintered Si3N4/BN Composite Ceramics with La2O3-Al2O3-Y2O3 as Sintering Additives

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Microstructure of hot-pressed h-BN/Si3N4 ceramic composites with Y2O3–Al2O3 sintering additive

Effect of Sintering Additive Content on Mechanical and Dielectric Properties of Porous Si3N4/BN Composite Ceramics

Effect of additions on the properties of Al2O3/BN machinable ceramics

Effects of additives to Si3N4 matrix on microstructure and properties of laminated Si3N4/BN ceramics

High Thermal Conductivity Silicon Nitride Ceramics Prepared By Pressureless Sintering With Ternary Sintering Additives

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Effect of Sintering Additive Composition on Microstructure and Mechanical Properties of Silicon Nitride

Effect of Hexagonal BN on the Microstructure and Mechanical Properties of Pressureless Sintered Porous Si3N4 Ceramics

Effect of Y2o3-Al2o3 Additive on the Phase Formation and Densification Process of in Situ Sic-Bn Composite

Effects of AlN content on phase composition, microstructure and mechanical properties of DN-based composite ceramics

Effect of B2O3 Addition on Low-temperature Sintering Behavior and Properties of SiC/h-BN Multiphase Ceramics

Tuning the electrical, thermal, and mechanical properties of SiC-BN composites using sintering additives

Mechanical properties and thermal shock resistance of Si2BC3N ceramics with ternary Al4SiC4 additive

Fabrication and Properties of SiO2-BN-Si3N4 Composites