Effect of AlN and ZrO2 on the Microstructure and Property of the 2Si-B-3c-n Ceramic
Pengfei Zhang,Bin Yang,Zhi Lu,Dechang Jia
DOI: https://doi.org/10.1016/j.ceramint.2017.11.134
IF: 5.532
2018-01-01
Ceramics International
Abstract:The mechanically-alloyed amorphous 2Si-B-3C-N powder was hot pressed at 1900°C for 30mins in argon. A small amount (5mol.%) of AlN and ZrO2 was added to investigate their effect on the sintering process, microstructure and properties of the 2Si-B-3C-N ceramic. XRD, SEM, TEM and property testing results show that, the addition of AlN or ZrO2 promotes the sintering process of the 2Si-B-3C-N composite powder, accelerates the crystallization and grain growth, and improves the density and mechanical properties of the prepared ceramic. Under an axial pressure of 80MPa and a gas pressure of 8bar, significant densification occurs to the 2Si-B-3C-N ceramic free from any additives just when the temperature is higher than 1830°C. The addition of AlN and ZrO2 decreases this critical temperature to about 1760°C and 1730°C, respectively. As a result, for the prepared bulk ceramic, the average grain size is increased from 80nm to 200nm and 250nm, the relative density is enhanced from 88.7% to 96.9% and 97.7%, and the bending strength is improved from 331MPa to 416MPa and 575MPa, respectively. Careful investigation reveals that in the prepared bulk ceramic, AlN forms solid solution with SiC, and ZrO2 exists in the form of t-ZrO2 and m-ZrO2 nanocrystals. Thus, the addition of AlN and ZrO2 may facilitate the atomic diffusion, the grain growth and the densification process of the 2Si-B-3C-N ceramic in difficult ways.