Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Synthesis of MgO-CaO-Al 2 O 3 -Sio 2 Nanocomposite Powder by Polymeric Complex Method As a Novel Sintering Additive of AlN Ceramics

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Novel precursor-derived Al–C–N–(O)-based ceramic additive for the low-temperature pressureless sintering of silicon nitride

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

Densification and Mechanical Properties of Si3N4/SiC Nanocomposite Using Si-Nitrided Si3N4 Powder

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Low-Temperature Sintering of AlN Ceramics by Sm 2 O 3 -Y 2 O 3 -Cao Sintering Additives Formed Via Decomposition of Nitrate Solutions

A New Sintering Additive for Silicon Carbide Ceramic

Effect of Multi-Sintering Additive MgO-Al2O3-CeO2 on Densification and Properties of Silicon Nitride Ceramics by Spark Plasma Sintering

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Combustion Synthesis of MgSiN2 Powders and Si3N4‐MgSiN2 Composite Powders: Effects of Processing Parameters

Composite Nitride Nanoceramics in the System Titanium Nitride (TiN)-Aluminum Nitride (AlN) through High Pressure and High Temperature Sintering of Synthesis-Mixed Nanocrystalline Powders

Low-temperature sintering of Al2O3 ceramics doped with 4CuO-TiO2-2Nb2O5 composite oxide sintering aid

A novel sintering additive system for porous mullite-bonded SiC ceramics: High mechanical performance with controllable pore structure

Novel fabrication process of AlN ceramic matrix composites at low temperatures

Synthesis of SiC-AlN Powder and Characterization of Its HIP-Sintered Compacts.

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Low -temperature sintering of Al<sub>2</sub>O<sub>3</sub> ceramics doped with 4CuO-Ti O<sub>2</sub>-2Nb<sub>2</sub>O<sub>5</sub> composite oxide sintering aid

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

Effects of MgAl2O4-ZrO2 Addition on Sintering Behaviors and Mechanical Properties of Silicon Nitride Ceramics

Research on the Densification Process of the Mechanically-Alloyed Amorphous 2Si-B-3c-n Powder