Abstract:The Mg-Al-RE series heat-resistant magnesium alloys are applied in automotive engine and transmission system components due to their high-temperature performance. However, after serving at a high temperature for a long time, the Al11RE3 phase coarsened and even decomposed, while the Mg17Al12 phase grew and dissolved, which limits the service temperature of Mg-Al-RE series heat-resistant magnesium alloys to a maximum of 175 °C. In this study, a new preparation method for in situ AlN particles was presented. The AlN/Mg-4Al-4La-0.3Mn composites were prepared by a master alloy and casting method. The effects of various contents of AlN (0.5-3.0 wt.%) on the microstructure and mechanical properties of the Mg-4Al-4La-0.3Mn (AE44) alloy at room (25 °C) and high temperatures (150-250 °C) were investigated. Microstructure analysis revealed that the inclusion of AlN led to a reduction in both the grain size and second phase size in the AE44 alloy, while also improving the distribution of the second phase. The average grain size, Al11La3 phase, Al2La phase, and Al3La phase of the 2.0 wt.% AlN/AE44 composite were 135.7, 9.6, 1.9, and 12.6 μm, respectively, which were significantly lower than those of the AE44 matrix alloy (179.8, 12.6, 3.3, 17.8 μm). The refinement was attributed to the ability of AlN particles to serve as heterogeneous nucleation cores for α-Mg and, at the same time, impede the growth of the solid-liquid interface, eventually leading to grain refinement. With the increase in the AlN content, the mechanical properties of composites initially exhibited an increase at both room and high temperatures, followed by a subsequent decrease. When the AlN content was 2.0 wt.%, the composite exhibited optimal strength and plasticity matching. At room temperature, the TYS, UTS, and EL values of the 2.0 wt.% Mg-4Al-4La-0.3Mn composite were 96 MPa, 175 MPa, and 7.0%, respectively, which were increased by 26 MPa, 27 MPa, and 0.7% when compared with the base alloy. The TYS of the 2.0 wt.% Mg-4Al-4La-0.3Mn composite at 150 °C, 200 °C, and 250 °C were 17 MPa, 14 MPa, and 22 MPa higher than those of the matrix alloy, respectively. The main strengthening mechanisms were second phase strengthening, load transfer strengthening, and thermal mismatch strengthening. At elevated temperatures, AlN particles effectively pinned the grain boundaries, inhibiting their migration, and hindered dislocation climbing, resulting in excellent mechanical properties of the composites at high temperatures. This study contributes to the advancement of in situ AlN particle preparation methods and the exploration of effects of AlN on the properties and microstructure of Mg-Al-RE alloys at high temperatures (150-250 °C).

Novel fabrication process of AlN ceramic matrix composites at low temperatures

Fabrication of Nanocrystalline Zro2 Particle Reinforced Aluminum Alloy Composite by Squeeze Casting Route

Enhanced Thermal and Dielectric Performance of Epoxy Resin/aluminum Nitride Nanocomposites at High Temperatures

Preparation of AlN microspheres/UHMWPE composites for insulating thermal conductors

Fabrication of High Thermal Conductivity Aluminum Nitride Ceramics via Digital Light Processing 3D Printing

Low Temperature Sintering and Performance of Aluminum Nitride/Borosilicate Glass

Impacts of Temperature and Time on Direct Nitridation of Aluminium Powders for Preparation of AlN Reinforcement

Microstructure and Mechanical Properties of Mg-Al-La-Mn Composites Reinforced by AlN Particles

In-situ formation of AlN/Al composite

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Thermal conductivities and mechanical properties of AlN ceramics fabricated by three dimensional printing

Fabrication of machinable AlN–BN composites with high thermal conductivity by pressureless sintering turbostatic BN-coated AlN nanocomposite powders

Effect of AlN on the Mechanical and Electrochemical Properties of Aluminum Metal Matrix Composites

High-temperature production of AlN in Mg alloys with ammonia gas

Composites of aluminum alloy and magnesium alloy with graphite showing low thermal expansion and high specific thermal conductivity

Improvement in mechanical properties in AlN-h-BN composites with high thermal conductivity

Microstructure of low-temperature sintered AlN

High-Thermal-Conductivity AlN Ceramics Prepared from Octyltrichlorosilane-Modified AlN Powder

In situ reaction mechanism of MgAlON in Al–Al2O3–MgO composites at 1700°C under flowing N2

Effect of Nanoaluminium Nitride Ceramic Particles on Microstructure, Mechanical Wear, and Machining Behavior of Al-Si-Mg Alloy Matrix Composites Produced by Bottom Pouring Type Stir Casting Route

Balancing thermal conductivity and strength of hot-pressed AlN ceramics via pre-sintering and annealing process