Abstract:A new type of non-oxide sintering additive of YH2 was introduced for the fabrication of AlN ceramics with high thermal conductivity and flexural strength. The effects of YH2 addition (0–5 wt%) on the phase composition, densification, microstructure, thermal conductivity and flexural strength of pressureless sintered AlN ceramics were investigated and compared with those Y2O3-added samples (1–5 wt%). The addition of 1 wt% YH2 led to an in-situ reduction reaction with oxygen impurities, the formation of Y2O3 and finally the formation of yttrium aluminate, which in turn improved densification and microstructure. A high flexural strength (408.69 ± 28.23 MPa) was achieved. The addition of 3 wt% YH2 increased the average grain size and purified the lattice. All these effects are believed to help achieve a high thermal conductivity of 184.82 ± 1.75 W·m−1·K−1. Although the thermal conductivity was close to the value of 3 wt% Y2O3-added sample, its strength was much increased to 381.53 ± 43.41 MPa. Meanwhile, it demonstrated a good combination of the thermal conductivity and flexural strength than the values reported in some literature. However, further increasing the YH2 addition to 5 wt% resulted in a high N/O ratio that inhibited the densification behavior of AlN ceramics. The current study showed that AlN ceramics with excellent thermal and mechanical properties could be obtained by the introduction of a suitable YH2 additive.

Transient Liquid-Phase Sintering And Thermal Conductivity Of Ain

Microstructure and thermal conductivity of aluminium nitride with (YCa)F3 as sintering aid

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Effects of binary additives B2O3–Y2O3 on the microstructure and thermal conductivity of aluminum nitride ceramics

Microstructure and thermal conductivity of aluminium nitride with (CaY)F3 as the sintering aid

Thermal Conductivity of AlN Ceramics Sintered with CaF2 and YF3

Microstructure and thermal conductivity of AlN ceramics with ultra-fine Y2O3 powder addition

Effects of Y2O3 and Yttrium Aluminates As Sintering Additives on the Thermal Conductivity of AlN Ceramic Substrates

Microstructure of low-temperature sintered AlN

Thermal Conductivity of AlN Ceramics with CaF2-YF3 Addition

Influence of stabilizing ions and sintering process on the thermal conductivity of alpha-SiAlON ceramics

Effects of Li2o on the Low Temperature Sintering and Thermal Conductivity of Aln Ceramics

Improving thermal conductivity of aluminum nitride ceramics by refining microstructure

Effect of Y2O3 on low temperature sintering and thermal conductivity of AlN ceramics

Mechanical Properties of AlN-SiC Ceramic Composites Synthesized by Pressureless Sintering and Post-HIP Treatment.

Effect of YF3 on densification behavior and thermal conductivity of AlN ceramics with Y2O3–YF3 additives under reducing atmosphere

Enhanced Properties of Dense Aln Ceramics Via in Situ Reaction

Effect of CeO2, Dy2O3, Yb 2O3 and y2O3 additives on thermal conductivity of silicon nitride ceramics

Effects of YH2 addition on pressureless sintered AlN ceramics

Effect of Post-Sintering Heat-Treatment on Thermal Conductivity of Si3N4 Ceramics Containing Different Additives

Sintering And Mechanical Properties Of Aln-Rich Ceramics In The Sic-Aln System