Abstract:The preparation of Ni–P–B coatings on surface of quartz optical fibers was carried out using electroless plating method. The effects of the concentrations of nickel chloride, sodium hypophosphite, potassium borohydride, ethylenediamine, cadmium sulfate and temperature on the quality of Ni–P–B coatings were investigated by orthogonal experiment and their optimal values were determined to be: 0.1molL−1, 0.094molL−1, 0.185molL−1, 0.36molL−1, 5.68×10−4molL−1 and 90°C, respectively. The effect of coarsening time of the naked fiber on the quality of Ni–P–B coatings was also researched and the optimal coarsening time was determined to be 15min. Stereomicroscope, Scanning Electron Microscope and X-ray diffractometer were used to characterize the apparentness, morphology and structure of the prepared Ni–P–B coatings. Inductively Coupled Plasma-Atomic Emission Spectroscopy, Thermal Shock Method and Gravimetric Analysis Method were employed to analyze the composition, force of adhesion and solderability of the coatings, respectively. The results showed that a Ni–P–B coating with low surface roughness, good strength of adhesion, low resistivity and good solderability was successfully prepared. The kinetic models (Ni–P–B deposition rate equations) of the process were established as v=7.95×10-6cA0.830cB0.428cC-0.288cD-0.645cE0..02exp26788(T-298)298RT;v=1.03×10-7cA0.830cB0.428cC-0.288cD-0.645cE-0.614exp26788(T-298)298RT. The theoretical values calculated by the models were proved to be basically consistent with the practical measurements through experimental verification.

A Study of Electroless Ni-Co-Fe-P Plating on Glass Fibers

Effects Of Nh4f On Electroless Ni-P Plating Bath And Properties Of Coatings

Studies of electroless Ni–Co–P ternary alloy on glass fibers

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Study of Electroless Ni-Zn-P Alloy Plating from Acidic Bath

Electroplating of Ni_(70)Cu_(30) alloy from pyrophosphate bath

CHEMICAL PLATING MECHANISM IN ACID BATHS AND FABRICATION OF Ni-P COATING WITH HIGH P CONTENT

Study on Properties of Electroless Plating Nickel-phosphorus Bright Alloy Coating

Electroless Co-P Alloy Plating of Superfine Si3N4 Powders

Effects of Ligands on Electroless Ni–P Alloy Plating from Alkaline Citrate–ammonia Solution

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

A Study of Electroless Ni Plating on SiCp/Al Composite Materials

Electroless Plating of Cu–Ni–P Alloy on PET Fabrics and Effect of Plating Parameters on the Properties of Conductive Fabrics

ZINC-NICKEL ALLOY ELECTROPLATING IN AN ALKALINE BATH

Process and Deposit Characterization of Electroless Ni-P-B Plating on the Surface of Quartz Optical Fiber

Optimization and kinetics of electroless Ni–P–B plating of quartz optical fiber

Study on Direct-Current Electroplated Ni-W-P Layer

Preparation of Amorphous Nickel-Phosphorus Alloy Coating by Electroplating

Optimization of the Electroplating Process for Amorphous Nickel- Phosphorus Alloy

A Method for Electroless Nickel Plating on Aluminum Alloy Surface

Electroless Plating of Ni–P Coatings on Carbon Steel in a Stirred Bed of Glass Balls