Study on Properties of Electroless Plating Nickel-phosphorus Bright Alloy Coating

HE Xue-feng,YING Hua-gen,YAN Mi

DOI: https://doi.org/10.3969/j.issn.1001-3849.2006.05.002

2006-01-01

Abstract:A compound brightener agent consisting of sodium benzene sulphinate,pyridine and sodium allyl sulphonate was added in the nickel-phosphorus electroless plating bath,and bright coatings can be obtained from the bath.In order to study the deposition process of electroless Ni-P plating with the addition of the brightener,the surface morphology and microstructure of coatings were characterized using the SEM.The phosphorus content in the coating was measured using spectrophotometry.Polarization curves of the ordinary coatings and the bright coatings in 3.5% NaCl solution were examined and the results were compared with that of neutral salt spray test.The results show that,compared with the ordinary coatings,the cystiform and the grain size of the bright coatings are decreased,and the phosphorus content is increased.The polarization curves and the neutral salt spray test result exhibit that the corrosion resistance of the bright coatings is increased.