Abstract:This study investigated the successful performance of acidic electroless Ni–P coatings on brass alloy from the nickel sulphamate bath. Three complexing agents (i.e., sodium acetate, acetic acid, and sodium citrate) were evaluated in a practical optimized sulphamate bath. Then, the corrosion behavior of coated samples was studied by potentiodynamic polarization (DC) and electrochemical impedance spectroscopy (EIS) methods in a 3.5 wt% NaCl solution. Moreover, the structure and chemical composition of the coated samples were characterized by X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS), respectively. In addition, the morphology of the coatings was examined through scanning electron microscopy (SEM), as well as investigating properties such as thickness, grain size, and actual capacitance using computational methods. The results revealed that the structure and corrosion behavior of coatings were strongly influenced by both practical conditions and complexing agent factors. Low and medium phosphorus coatings with nanocrystalline and semi-crystalline structures were developed according to EDS and XRD results. Additionally, SEM images and electrochemical results demonstrated low phosphorous Ni–P coatings from baths containing sodium acetate with a cauliflower structure, as well as an acetic acid complexing agent with a dense structure and highly acceptable granulation which had the best anti-corrosion behavior ( R P = 46,369 Ω cm 2 & i corr= 0.56 and R P = 44,561 Ω cm 2 & i corr= 0.7 , respectively) compared to a bare sample ( R p = 3687 Ω cm 2 & i corr= 2.72 ).

Effects of Ligands on Electroless Ni–P Alloy Plating from Alkaline Citrate–ammonia Solution

Effects Of Nh4f On Electroless Ni-P Plating Bath And Properties Of Coatings

Effects of Surfactants in an Electroless Nickel-Plating Bath on the Properties of Ni−P Alloy Deposits

Electrochemical Synthesis and Characterization of Ni–P Alloy Coatings from Eutectic–Based Ionic Liquid

CHEMICAL PLATING MECHANISM IN ACID BATHS AND FABRICATION OF Ni-P COATING WITH HIGH P CONTENT

Effects of NH4F on the deposition rate and buffering capability of electroless Ni–P plating solution

Effect of nickel immersion pretreatment on the corrosion performance of electroless deposited Ni–P alloys on aluminum

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

A Method for Electroless Nickel Plating on Aluminum Alloy Surface

Ni-P coatings electroplating - A review, Part I: Pure Ni-P alloy

Studies of electroless Ni–Co–P ternary alloy on glass fibers

Study on Properties of Electroless Plating Nickel-phosphorus Bright Alloy Coating

Study on Electroless Plating Ni-W-P Ternary Alloy with High Tungsten from Compound Complexant Bath

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

Preparation of Amorphous Nickel-Phosphorus Alloy Coating by Electroplating

The Effect of Complexing Agent on Electroless Nickel Sulphamate Coating on Brass Alloy: Structure Characteristics & Corrosion Behavior

Composite Electroless Nickel-nano Al2O3 Coatings on Steel Substrate

The Research on Coating of Electroless Ni-W-P Ternary Alloys

Optimization of the Electroplating Process for Amorphous Nickel- Phosphorus Alloy

Structure, Composition and Corrosion Resistance of Zn-Ni-P Alloys Electrodeposited from an Ionic Liquid Based on Choline Chloride

High Hardness and Wear Resistance Electroless Ni-P Deposits Without Heat Treatment