Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

WU Lei,YING Hua-gen,WU Jin-ming,LUO Wei,YAN Mi

DOI: https://doi.org/10.3969/j.issn.1001-4381.2006.z1.054

2006-01-01

Abstract:Electroless Ni-Co-P ternary alloy deposits were prepared by optimizing the bath composition and operating conditions to improve the corrosion resistance of NdFeB permanent magnets. The effects of pH and metallic ion ratio([Co2+]/[Ni2+ +Co2+]) on plating rate and deposit composition were investigated. Polarization curves of NdFeB matrix with and without Ni-Co-P deposits in 3.5% (mass fraction)NaCl solution were examined. It is found that the plating rate and the cobalt content of the deposit increase with increasing pH, while the nickel and phosphorus contents decrease. With increasing metallic ratio, the plating rate decreases and the cobalt content of the deposit increases with a simultaneous decrease in the nickel and phosphorus contents. The polarization curves exhibit that the corrosion rate of NdFeB magnets decreases by two orders of magnitude in 3.5% NaCl solution after electroless plating with the Ni-Co-P deposits. The use of the metallic ion ratio at 0. 3 in the bath solution could achieve the best corrosion resistance.