Abstract:Fe-Co-Ni coating, a vital type of transition metal alloy, shows great potential in the field of hydrogen storage and magnetic materials. In this study, Fe-Co-Ni coatings were prepared on Cu substrates from a deep eutectic solution of choline chloride/2Urea (ChCl/2Urea) DES by electrodeposition. The effects of deposition potential on the morphology, chemical composition, crystal structure, corrosion resistance and magnetic properties of nanostructured Fe-Co-Ni coatings were investigated. The results revealed that the reduction process of Fe-Co-Ni alloy on the Cu electrode in ChCl/2Urea DES was irreversible three-dimensional instantaneous nucleation, which was controlled by diffusion. The surface morphology, microstructure, compose and crystallite size of the Fe-Ni-Co alloy were related to the deposition potential. The Fe content of the electrodeposited alloys showed a maximum of 48.17 at% at the applied potential of −1.3 V and a positive correlation was observed between the Fe content and electrodeposition potential in the investigated potential range. The nickel-rich coatings were obtained at high potential and iron-rich coatings were obtained at low potential. The less roughness, more compact grain and uniform flat Fe-Co-Ni coatings were prepared under a more negative potential. The Fe-Co-Ni coatings were composed of face-centered cube (fcc, NiFe) and body-centered cube crystals (bcc, FeCo). With the negative shift of deposition potential, the structure of Fe-Co-Ni coatings grew preferentially toward FeCo(110) and FeCo(211) crystal surfaces. The Fe-Co-Ni coatings prepared from ChCl/2Urea DES at different deposition potentials showed good corrosion resistance. Fe-Co-Ni coating that is produced at the deposition potential of −1.2 V, exhibited a more positive corrosion potential and obvious magnetic anisotropy.

Electrodeposition and corrosion performance of Ni-Co alloys with different cobalt contents

Electrodeposition of Ni–Co alloys from a deep eutectic solvent

Effect of cobalt content on electrodeposition and properties of Co–Ni alloy thin films

Microstructure and tribological properties of electrodeposited Ni–Co alloy deposits

Influences of Co and process parameters on structure and corrosion properties of nanocrystalline Ni-W-Co ternary alloy film fabricated by electrodeposition at low current density

Effect of Cobalt Content on the Properties of Nickel-Cobalt Alloy Coatings

Codeposition Behavior of Fe-Ni Alloys: A Review in Mechanisms, Preparation and Effects on Composition

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Influence of the material processing on the electrochemical properties of cobalt-free Ml(NiMnAlFe)5 alloy

Deposition of Ni–Co by cyclic voltammetry method and its electrocatalytic properties for oxygen evolution reaction

Preparation of thin solid CoNiFe films by pulse-reverse electroplating technique

Effect of adding mode of cobalt on the electrochemical performance of a-Ni(OH)(2)

Effect of Α-Al2o3 Particles on the Electrochemical Codeposition of Co–Ni Alloys from Sulfamate Electrolytes

Influence Of Alpha-Al2o3 Nanoparticles On The Anomalous Electrodeposition Of Co-Ni Alloys

Electrodeposition and characterization of nanocrystalline CoNiFe films

Effects of Metallic Cobalt Addition on the Performance of Pasted Nickel Electrodes

Electroplating of Nanocrystalline Ni–Co Alloys Using Cysteine and Their Electrochemical Behaviour in NaOH Solution

Electroplating and characterization of Zn–Ni, Zn–Co and Zn–Ni–Co alloys

Electrochemical corrosion behaviors and corrosion protection properties of Ni–Co alloy coating prepared on sintered NdFeB permanent magnet

Electrochemical behavior and electrodeposition of Fe-Co-Ni thin films in choline chloride/urea deep eutectic solvent

Microstructure and electrochemical properties of cobalt-substituted A2B7-type La–Y–Ni-based hydrogen storage alloys