Abstract:The electrical resistivity and the anisotropic magnetoresistance (AMR) was investigated for Ni Co alloys at and below room temperature. The Ni Co alloy layers having a thickness of about 2 um were prepared by electrodeposition on Si wafers with evaporated Cr and Cu underlayers. The alloy composition was varied in the whole concentration range by varying the ratio of Ni sulfate and Co sulfate in the electrolyte. The Ni Co alloy deposits were investigated first in the as deposited state on the substrates and then, by mechanically stripping them from the substrates, as self supporting layers both without and after annealing. According to an X ray diffraction study, a strongly textured face centered cubic (fcc) structure was formed in the as deposited state with an average grain size of about 10 nm. Upon annealing, the crystal structure was retained whereas the grain size increased by a factor of 3 to 5, depending on alloy composition. The zero field resistivity decreased strongly by annealing due to the increased grain size. The annealing hardly changed the AMR below 50 at.% Co but strongly decreased it above this concentration. The composition dependence of the resistivity and the AMR of the annealed Ni Co alloy deposits was in good quantitative agreement with the available literature data both at 13 K and at room temperature. Both transport parameters were found to exhibit a pronounced maximum in the composition range between 20 and 30 at.% Co and the data of the Ni Co alloys fit well to the limiting values of the pure component metals (fcc Ni and fcc Co). The only theoretical calculation reported formerly on fcc Ni Co alloys yielded at T=0K a resistivity value smaller by a factor of 5 and an AMR value larger by a factor of about 2 than the corresponding low temperature experimental data, although the theoretical results properly reproduced the composition dependence of both quantities.

Effect of cobalt content on electrodeposition and properties of Co–Ni alloy thin films

Electrodeposition and corrosion performance of Ni-Co alloys with different cobalt contents

Electrodeposition of Ni–Co alloys from a deep eutectic solvent

Structural, Morphological, and Magnetic Properties of Electrodeposited CoNi Thin Films on the FTO Substrate

Influences of Co and process parameters on structure and corrosion properties of nanocrystalline Ni-W-Co ternary alloy film fabricated by electrodeposition at low current density

Microstructure and tribological properties of electrodeposited Ni–Co alloy deposits

Effect of Cobalt Content on the Properties of Nickel-Cobalt Alloy Coatings

Electrochemical behavior and electrodeposition of Fe-Co-Ni thin films in choline chloride/urea deep eutectic solvent

Influence Of Alpha-Al2o3 Nanoparticles On The Anomalous Electrodeposition Of Co-Ni Alloys

Effect of Α-Al2o3 Particles on the Electrochemical Codeposition of Co–Ni Alloys from Sulfamate Electrolytes

Electrodeposition and characterization of nanocrystalline CoNiFe films

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Codeposition Behavior of Fe-Ni Alloys: A Review in Mechanisms, Preparation and Effects on Composition

Influence of the material processing on the electrochemical properties of cobalt-free Ml(NiMnAlFe)5 alloy

Influence of deposition parameters on the electrodeposited ternary CoFeCu coatings

Effect of Electroplating Bath Composition on Corrosion Resistance of Deposited Cobalt Films

Electroplating and characterization of Zn–Ni, Zn–Co and Zn–Ni–Co alloys

Electroplating of Nanocrystalline Ni–Co Alloys Using Cysteine and Their Electrochemical Behaviour in NaOH Solution

Temperature dependence of the electrical resistivity and the anisotropic magnetoresistance (AMR) of electrodeposited Ni Co alloys

Microstructure and Properties of Electrodeposited Nanocrystalline Ni-Co-Fe Coatings

Evaluation of corrosion resistance of electrodeposited nanocrystalline Ni–Fe alloy coatings