Abstract:Sintered NdFeB magnets are being utilised in numerous applications because of the excellent magnetic properties. However, due to its main components are Fe, B and rare earth metals. There is a potential difference between the neodymium rich phase, boron rich phase and the main phase, which was very easy to form a primary battery and cause electrochemical corrosion on the surface of the material. After the materials are easy to be corroded or the components and structures change, the performance of the materials will become weak or even lost, which will affect the service performance and life of the devices or equipment. According to the requirements of surface protection technology for NdFeB magnets, the preparation of protective coating by magnetron sputtering was an efficient means to enhance the corrosion resistance of magnets. Pure Al coating was deficient in microstructure, hardness and corrosion resistance, and the preparation of composite coating by doping co-sputtering had become a development trend. In the current work, AlTi coatings with various Ti contents were prepared from an Al target and a Ti target using direct and radio frequency hybrid magnetron co-sputtering. The surface morphology, microstructure, and elemental compositions of the AlTi coatings were explored through XRD (X-ray diffraction), SEM (scanning electron microscopy), and EDS (energy dispersive spectroscopy). The anticorrosion performances of the AlTi coatings were evaluated by performing electrochemical tests. According to SEM and EDS, the AlTi composite coating was denser and more homogeneous than that of the Al single layer. Furthermore, the results demonstrated that microcrystalline Ti doping reduced the grain size of Al coatings. Therefore, the corrosion current density of the sintered NdFeB magnets plated with Al(120w)/Ti(10w) was approximately more than a hundred times inferior to that of the pure Al layer, and the hardness of AlTi composite coatings also improved.

Amorphous Al–Mn Coating on NdFeB Magnets: Electrodeposition from AlCl3–EMIC–MnCl2 Ionic Liquid and Its Corrosion Behavior

Al–Mn coating electrodeposited from ionic liquid on NdFeB magnet with high hardness and corrosion resistance

Corrosion Resistance of Electrodeposited Aluminum Coating on NdFeB Magnet from AlCl_3-EMIC Ionic Liquid

Corrosion Protection of Nd-Fe-B Sintered Magnets by Aluminum Coating

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

Microstructure and Corrosion Resistance of Aluminum Coating Electrodeposited on NdFeB Magnet from Ionic Liquid

Electrodeposition of bright Al and Al-Mn coatings from AlCl3-EMIC ionic liquid

Viscous Layer Formed in the Anodic Electrolytic Etching of Reactive Metals in Ionic Liquid

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Microstructure, corrosion resistance and formation mechanism of alumina micro-arc oxidation coatings on sintered NdFeB permanent magnets

Morphology and Anti-Corrosive Performance of Cr(III) Passivated Zn-Fe Alloy Coating on NdFeB Substrate

Electrodeposition of amorphous Ni–P coatings onto Nd–Fe–B permanent magnet substrates

Formation of aluminide coatings by low-temperature heat treatment of Al coating electrodeposited from ionic liquid

Effects of Pulsed-Electrodeposition Parameters on the Property of Aluminum Film Onto Sintered Ndfeb Magnets

Electrochemical corrosion behaviors and corrosion protection properties of Ni–Co alloy coating prepared on sintered NdFeB permanent magnet

Electrodeposition of aluminum on rare earth alloy surface in room temperature molten salts

Anodic Behavior of Neodymium in Acidic AlCl_3-1-ethyl-3-methyl-imidazolium Chloride Ionic Liquid

Effect of Potential on Aluminium Early-Stage Electrodeposition Onto Ndfeb Magnet

Densification and anticorrosion performances of vacuum evaporated aluminium coatings on NdFeB magnets

Fabrication and Properties of Micro-arc Oxidation Coatings on Sintered NdFeB Permanent Magnets

Microstructures of Al coatings prepared through magnetron co-sputtering with microcrystalline Ti doping