Abstract:In this study, a protective Ni–Co alloy coating was prepared on sintered NdFeB magnet applying electrodeposition technique. A pure nickel coating was also studied for a comparison. The microstructure, surface morphologies, and chemical composition of coatings were investigated using X-ray diffraction, scanning electron microscope, and energy dispersive spectroscopy, respectively. The corrosion protection properties of coatings for NdFeB magnet in neutral 3.5 wt.% NaCl solutions were evaluated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques. The microstructure and surface morphologies analysis showed that the addition of cobalt element into matrix metal Ni altered the preferential orientation of pure nickel coating from (2 0 0) crystal face for pure nickel coating to (1 1 1) crystal face for Ni–Co alloy coating, and made the surface morphologies more compact and uniform due to the grain-refining. The results of potentiodynamic polarization test showed that compared with pure nickel coating, Ni–Co alloy coating exhibited much nobler corrosion potential (Ecorr) and lower corrosion current density (jcorr), indicating better anticorrosive properties. The long-term immersion test by dint of EIS indicated that the Ni–Co alloy coating still presented high impedance value of 1.9 × 105 Ω cm2 with the immersion time of 576 h indicating the excellent anticorrosive properties, and corrosion protection properties of nickel coating for NdFeB magnet practically disappeared with the immersion time of 144 h, which also indicated that the Ni–Co alloy coating provided better corrosion protection properties for the NdFeB magnet compared with nickel coating.

Electroless Ni-Co-P Coatings on Sintered Nd-Fe-B Magnets with Improved Corrosion Resistance

Study Magnetic Properties and Corrosion Resistance of Sintered NdFeBAlDyNb Magnets

EFFECTS OF ULTRASONIC ELECTROLESS Ni- P PLATING ON THE CORROSION RESISTANCE OF SINTERED NdFeB MAGNETS

Corrosion Protection of Nd-Fe-B Sintered Magnets by Aluminum Coating

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

Preparation of coatings with high adhesion strength and high corrosion resistance on sintered Nd–Fe–B magnets through electroless plating

Effects of Nd3+ on adhesion and corrosion resistance of electroless Ni-P coating on sintered Nd-Fe-B magnets

Corrosion behavior of Nd-Fe-B sintered magnets at remanence state

Electrochemical corrosion behaviors and corrosion protection properties of Ni–Co alloy coating prepared on sintered NdFeB permanent magnet

Corrosion Behavior of Sintered NdFeB Magnets Coated with Ni Coatings Deposited by Ion Beam Sputtering

Corrosion behavior and strengthening mechanism of Ni-Cu alloy coating on Nd-Fe-B magnets

Amorphous Al–Mn Coating on NdFeB Magnets: Electrodeposition from AlCl3–EMIC–MnCl2 Ionic Liquid and Its Corrosion Behavior

Corrosion Resistance of Nd–Fe–B Sintered Magnets with Intergranular Addition of Cu60Zn40 Powders

Improvement of corrosion resistance of Cu and Nb co-added Nd–Fe–B sintered magnets

Fabrication and Properties of Micro-arc Oxidation Coatings on Sintered NdFeB Permanent Magnets

Magnetic properties and corrosion resistance of Nd–Fe–B magnets with Nd64Co36 intergranular addition

Electrochemical Corrosion Behavior of Hot-Deformed NdFeB Magnet with Different Content of Nano-Tic

A design of sintered Nd-Fe-B magnet exhibiting superior corrosion resistance based on the metallurgical behavior of Ni and Cr

Improved corrosion resistance of low rare-earth Nd–Fe–B sintered magnets by Nd6Co13Cu grain boundary restructuring

Effects of Cu Nanopowders Addition on Magnetic Properties and Corrosion Resistance of Sintered Nd–Fe–B Magnets