Abstract:Sintered NdFeB magnets are being utilised in numerous applications because of the excellent magnetic properties. However, due to its main components are Fe, B and rare earth metals. There is a potential difference between the neodymium rich phase, boron rich phase and the main phase, which was very easy to form a primary battery and cause electrochemical corrosion on the surface of the material. After the materials are easy to be corroded or the components and structures change, the performance of the materials will become weak or even lost, which will affect the service performance and life of the devices or equipment. According to the requirements of surface protection technology for NdFeB magnets, the preparation of protective coating by magnetron sputtering was an efficient means to enhance the corrosion resistance of magnets. Pure Al coating was deficient in microstructure, hardness and corrosion resistance, and the preparation of composite coating by doping co-sputtering had become a development trend. In the current work, AlTi coatings with various Ti contents were prepared from an Al target and a Ti target using direct and radio frequency hybrid magnetron co-sputtering. The surface morphology, microstructure, and elemental compositions of the AlTi coatings were explored through XRD (X-ray diffraction), SEM (scanning electron microscopy), and EDS (energy dispersive spectroscopy). The anticorrosion performances of the AlTi coatings were evaluated by performing electrochemical tests. According to SEM and EDS, the AlTi composite coating was denser and more homogeneous than that of the Al single layer. Furthermore, the results demonstrated that microcrystalline Ti doping reduced the grain size of Al coatings. Therefore, the corrosion current density of the sintered NdFeB magnets plated with Al(120w)/Ti(10w) was approximately more than a hundred times inferior to that of the pure Al layer, and the hardness of AlTi composite coatings also improved.

Electrochemical Corrosion Behavior of Hot-Deformed NdFeB Magnet with Different Content of Nano-Tic

Study Magnetic Properties and Corrosion Resistance of Sintered NdFeBAlDyNb Magnets

Corrosion Protection of Nd-Fe-B Sintered Magnets by Aluminum Coating

Relations of Magnetic and Electrochemical Anti-Corrosion Properties of (zr, Ti)-doped NdCeFeB Magnets with Ti Content

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Electroless Ni-Co-P Coatings on Sintered Nd-Fe-B Magnets with Improved Corrosion Resistance

Bending strength improvement of sintered Nd-Fe-B alloy via strengthening triple junction phase by nano-TiC

Magnetic Properties and Microstructure Evolution of In-Situ Tb-Cu Diffusion Treated Hot-Deformed Nd-Fe-B Magnets

Corrosion Resistance of Nd–Fe–B Sintered Magnets with Intergranular Addition of Cu60Zn40 Powders

Effects of Nd3+ on adhesion and corrosion resistance of electroless Ni-P coating on sintered Nd-Fe-B magnets

Improvement of the coercivity and corrosion resistance of Nd–Fe–B sintered magnets by intergranular addition of Tb62.5Co37.5

Corrosion Behavior of Al100−xCux (15≤x≤45) Doped Nd–Fe–B Magnets

Improvement of coercivity and its thermal stability of hot-deformed Nd-Fe-B magnets processed by Tb<sub>70</sub>Cu<sub>30</sub> doping and subsequent Nd<sub>85</sub>Cu<sub>15</sub> diffusion

Effect of nano-Cu addition on the diffusion behaviors of Dy in hot-deformed Nd-Fe-B magnets

Effects of Cu Nanopowders Addition on Magnetic Properties and Corrosion Resistance of Sintered Nd–Fe–B Magnets

Corrosion Behavior of Sintered NdFeB Magnets Coated with Ni Coatings Deposited by Ion Beam Sputtering

Understanding the role of Cu element in nanocrystalline hot deformed Nd-Fe-B magnets

Improvement of coercivity and its thermal stability of hot-deformed Nd-Fe-B magnets processed by Tb70Cu30 doping and subsequent Nd85Cu15 diffusion

Microstructures of Al coatings prepared through magnetron co-sputtering with microcrystalline Ti doping

Corrosion Behavior of Hot-Pressed Nanocrystalline Ndfeb Magnet in A Simulated Marine Atmosphere