Relations of Magnetic and Electrochemical Anti-Corrosion Properties of (zr, Ti)-doped NdCeFeB Magnets with Ti Content

Yuxuan Shao,Junjie Ni,Zhiwei Wang,Xuegeng Wang,Kai Xu,Bo Song,Yue Xu,Shutai Zhou,Tao Liu,Laima Luo

DOI: https://doi.org/10.1016/j.jmrt.2024.10.120

2024-01-01

Abstract:Zr and Ti were co-doped into NdCeFeB sintered magnets to improve the magnetic and electrochemical anticorrosion properties. Both performance are found closely associated with Ti content. At 0.15 wt%Ti, the sample shows higher coercivity without energy product loss compared to the Ti-free sample and other Ti additions, due to the matrix-phases refinement and optimized distribution of RE-rich phases. For this sample, its corrosion current density and charge transfer resistance are 1.94 mu A/cm2 and 1734 Omega center dot cm2 in NaCl solution respectively, which exhibits obviously improved corrosion resistance in comparison with the Ti-free magnet. The charge transfer resistance has been increased by 45.6 %. The apparently improved corrosion resistance is mainly attributed to the decreased amount of active reaction channels and the enhanced protective effect of TiO2, arising from the increment of Ti-rich precipitates. When the content of Ti dopant exceeds 0.5 wt%, the beneficial effects of Ti are overshadowed by the harmful effect of the density reduction on anti-corrosion performance, and the charge transfer resistance decreased with further increasing the dopant content. The new findings provide a theoretical basis for improving physicochemical properties of NdCeFeB magnet.