Abstract:Nanocrystalline Ni-Mo alloy coatings with excellent brightness, high hardness, and corrosion resistance were prepared. Nanocrystalline Ni-Mo alloy coating with a Mo content of 14.94 at% was electrodeposited on the copper foil substrate under the optimized conditions with the current efficiency of 51.64%. The electrodeposition behavior of Ni-Mo alloy coatings was studied by cathodic polarization curve and chronopotentiometry. Chronopotentiometry showed that the nucleation rate of Ni-Mo alloys can be accelerated with the increase of current density. Meanwhile, the cathodic polarization curves show that the additives can effectively inhibit the electrodeposition of Ni-Mo alloys. The (2 0 0) and (2 2 0) diffraction peaks of Ni gradually disappeared and the grain size gradually decreased with the increase of Mo content in the alloy coating according to XRD and TEM analysis. Scanning electron microscope (SEM) and confocal microscope observation results show that the coating becomes smoother and denser with the increase of Mo content when Mo content was lower than 14.94 at%, after which the density of the coating saw a decline due to the intensified hydrogen evolution reaction. The microhardness results of the alloy coating show that the microhardness of the alloy coating is related to the solid solution strengthening, texture evolution, and plastic deformation of the alloy. Meanwhile, the alloy coating has a Hall-Petch relationship and inverse Hall-Petch relationship, and the critical grain size is 5.5 nm. The corrosion resistance of Ni-Mo alloy coating is better than that of pure Ni coating, and the corrosion resistance is optimal when the Mo content is about 15 at%. In addition, in the plating solution containing additives, the deposited Ni-Mo alloy coating is smoother and denser, and the hardness and corrosion resistance of the alloy coating is also greatly improved.

Studies of electroless Ni–Co–P ternary alloy on glass fibers

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

The Research on Coating of Electroless Ni-W-P Ternary Alloys

Electrochemical Synthesis and Characterization of Ni–P Alloy Coatings from Eutectic–Based Ionic Liquid

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Co–Al2O3 nanocomposites powder prepared by electroless plating

A Study of Electroless Ni Plating on SiCp/Al Composite Materials

Effects of Ligands on Electroless Ni–P Alloy Plating from Alkaline Citrate–ammonia Solution

Study on Electroless Plating Ni-W-P Ternary Alloy with High Tungsten from Compound Complexant Bath

Electroless Co-P Alloy Plating of Superfine Si3N4 Powders

Studies on structure of electroless Ni-P alloy

Electrodeposition of Ni-W-P alloy

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Non-isothermal crystallization kinetics of amorphous electroless nickel-phosphorus alloy plating

Electrodeposition and corrosion performance of Ni-Co alloys with different cobalt contents

Electroless Ni-P-Sic Composite Coatings with Superfine Particles

Electrodeposition of nanocrystalline Ni-Mo alloys in pyrophosphate baths

Electrodeposition of Ni–Co alloys from a deep eutectic solvent

Model of electroless Ni deposition on SiC/Al composites and study of the interfacial interaction of coatings with substrate surface

Study on Properties of Electroless Plating Nickel-phosphorus Bright Alloy Coating

Electrodeposition of palladium films on Ni-Co coatings