Co–Al2O3 nanocomposites powder prepared by electroless plating

C. Zhang,G.P. Ling,J.H. He

DOI: https://doi.org/10.1016/S0167-577X(03)00445-2

IF: 3

2004-01-01

Materials Letters

Abstract:In this paper, a new type of Co–Al2O3 nanocomposites powder prepared by electroless plating technique will be introduced. The raw Al2O3 nanoparticles are 10–20 nm in diameter. The Co plating was carried out at middle temperature (45–50 °C) with application of ultrasonic radiation. Plating rate was determined by measuring the weight gain of powder after plating. High-resolution transmission electron microscopy (HRTEM) reveals that Co–Al2O3 nanocomposites particles is of nearly sphere-like shape and is about 50–60 nm in diameter. X-ray diffraction (XRD) indicates that the chemical composition of plating layer is Co–P alloy. The phase structure is different when the reductant content changed. Co–P alloy was found to be amorphous in as-plating Co–Al2O3 powder and was transformed into a crystalline phase after sintering. Differential scanning calorimeter (DSC) analysis proves that such a phase transformation occurs at 203–253 °C. Different Co–P content was obtained by changing the Al2O3 load.