Effects of Zr element on the microstructure and mechanical properties of B4C/Al composites fabricated by melt stirring method
Xizhou Kai,Lin Wu,Yanjie Peng,Zhanqiu Tan,Guirong Li,Gang Chen,Xiaojing Xu,Zhiqiang Li,Yutao Zhao
DOI: https://doi.org/10.1016/j.compositesb.2021.109156
2021-11-01
Abstract:<p>In this study, the addition of Zr element (K<sub>2</sub>ZrF<sub>6</sub>) was employed to improve the wettability, inhibit the serious chemical reaction of B<sub>4</sub>C to Al, and uniformly disperse the B<sub>4</sub>C particles in the Al melt, during the fabrication of B<sub>4</sub>C/Al composites via melt stirring method. And the particle distribution, interface microstructure and mechanical properties of the fabricated composites were further investigated. The metallography observation shows that the B<sub>4</sub>C particles could be effectively introduced to the Al melt with the addition of Zr element, while there were few B<sub>4</sub>C particles observed in the composites without Zr addition. The XRD analysis indicates that the ZrB<sub>2</sub> and ZrC peaks arise with the addition of Zr, where the ZrB<sub>2</sub> and ZrC have better chemical stabilization and wettability than the B<sub>4</sub>C ceramic particles. The SEM, EDS, TEM and SAED analysis shows that the ZrB<sub>2</sub> and ZrC interface layer with a thickness of about 200–350 nm on the B<sub>4</sub>C surface was formed, which could avoid the serious chemical reaction and improve the wettability of B<sub>4</sub>C to Al, simultaneously. In addition, the easy introduction of B<sub>4</sub>C particles to the Al melt with K<sub>2</sub>ZrF<sub>6</sub>, the formation mechanism of ZrB<sub>2</sub> and ZrC layer, and mechanical properties of the composites were also discussed.</p>
engineering, multidisciplinary,materials science, composites