Abstract:Al2O3-ZrO2-CeO2 composite coatings were prepared by plasma spraying Al2O3-ZrO2 composite powders with and without CeO2 addition. The microstructure and properties of the Al2O3-ZrO2-CeO2 coatings at high temperature and thermal shock resistance were investigated. The results show that an amorphous phase was formed in the plasma sprayed Al2O3-ZrO2 and Al2O3-ZrO2-CeO2 coatings. The Al2O3-ZrO2 coating consisted mainly of t-ZrO2, α-Al2O3, and γ-Al2O3. The Al2O3-ZrO2-CeO2 coating consisted mainly of t-ZrO2, α-Al2O3, γ-Al2O3, and CeO2. The Al2O3-ZrO2-CeO2 coating was more uniform and denser than the Al2O3-ZrO2 coating. The results after heat treatment showed that the two coatings were stable at 800 °C. With the increase of temperature, the coatings underwent phase transformation at high temperature (1000 and 1200 °C). At 1000 °C, the amorphous phase was obviously reduced, and the amorphous phase was crystallized to form nanocrystals. When the heat treatment temperature was raised to 1200 °C, the intensity of the diffraction peaks of t-ZrO2 and α-Al2O3 increased, the amorphous phase was completely crystallized, and γ-Al2O3 was transformed into α-Al2O3. The porosity of the two coatings decreased and the hardness increased after heat treatment. The thermal shock resistance of the coatings on the TC4 titanium alloy substrate was better than that on the Q235 steel substrate. The thermal shock resistance of the Al2O3-ZrO2-CeO2 coating was better than that of the Al2O3-ZrO2 coating.

Microstructure and mechanism of Al2O3-ZrO2 eutectic coating prepared by combustion-assisted thermal explosion spraying

The Microstructure of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

The Microstructure Evolution and Mechanical Properties of Al2O3/ZrO2 Coatings with Different ZrO2 Contents: Guidelines to Prepare Eutectic Powders

Microstructure of plasma-sprayed Al2O3-ZrO 2 composite coatings

MICROSTRUCTURE OF PLASMA-SPRAYED <font>Al</font><sub>2</sub><font>O</font><sub>3</sub>–<font>ZrO</font><sub>2</sub> COMPOSITE COATINGS

Microstructure and mechanical properties of eutectic composite ceramic Al2O3/ZrO2 by explosion synthesis

Preparation and Microstructure of Nanostructured Al2O3-ZrO2 Coating

Characterization of the Near-Eutectic Al2O3–40 Wt% ZrO2Composite Coating Fabricated by Atmospheric Plasma Spray. Part II: Microstructure and Mechanical Properties of Nanocomposite Coating

Characterization of the Near-Eutectic Al<sub>2</sub>O<sub>3</sub>–40 wt% ZrO<sub>2</sub>Composite Coating Fabricated by Atmospheric Plasma Spray. Part II: Microstructure and Mechanical Properties of Nanocomposite Coating

Ke ICROSTRUCTURE AND MECHANICAL PROPERTIES OF EUTECTIC COMPOSITE CERAMIC Al 2 O 3 / ZrO 2 BY EXPLOSION SYNTHESIS

Microstructure and property of Al2O3 coating for tuyere in blast furnace deposited by plasma spraying

Microstructure and abrasive resistance of ZrO2-MoSi2 coatings deposited by supersonic plasma spraying

Microstructure and properties of Al2O3–ZrO2–TiO2 composite coatings prepared by plasma spraying

Microstructure and tribological properties of Fe-based amorphous coating prepared by detonation spray

Microstructure and Properties of Al2O3-13wt.%TiO2-Reinforced CoCrFeMnNi High-Entropy Alloy Composite Coatings Prepared by Plasma Spraying

Fabrication and Microstructure of ZrO2/NiCrCoAlY Graded Coating by Plasma Spraying

Characterization of the Near-Eutectic Al2O3–40 Wt% ZrO2Composite Coating Fabricated by Atmospheric Plasma Spray. Part I: Preparation and Characterization of Nano Al2O3–ZrO2Powder Using Sol–Gel Method

Microstructure and Thermal Shock Resistance Property Research of FeMnCr/ZrO2 Composite Coating Deposited by High Velocity Arc Spraying

Preparation and Microstructures of CoAl(2)O(4) ZrO(2) Composite

Preparation and Flame Ablation Resistance of Al/Zn/Cu-Incorporated Yttria Partially Stabilized Zirconia Coating

High Temperature Microstructure Evolution and Thermal Shock Resistance of Plasma Sprayed Al2O3-ZrO2-CeO2 Coatings