Abstract:Zirconia sprayed coatings are widely used as thermal barrier coatings (TBC) for high temperature protection of metallic structures. However, their use in diesel engine combustion chamber components has the long run durability problems, such as the spallation at the interface between the coating and substrate due to the interface oxidation. Although zirconia coatings have been used in many applications, the interface spallation problem is still waiting to be solved under the critical conditions such as high temperature and high corrosion environment. The gas tunnel type plasma spraying developed by the author can make high quality ceramic coatings such as Al2O3 and ZrO2 coating compared to other plasma spraying method. A high hardness ceramic coating such as Al2O3 coating by the gas tunnel type plasma spraying, were investigated in the previous study. The Vickers hardness of the zirconia (ZrO2) coating increased with decreasing spraying distance, and a higher Vickers hardness of about Hv = 1200 could be obtained at a shorter spraying distance of L = 30 mm. ZrO2 coating formed has a high hardness layer at the surface side, which shows the graded functionality of hardness. In this study, ZrO2 composite coatings (TBCs) with Al2O3 were deposited on SS304 substrates by gas tunnel type plasma spraying. The performance such as the mechanical properties, thermal behavior and high temperature oxidation resistance of the functionally graded TBCs was investigated and discussed. The resultant coating samples with different spraying powders and thickness are compared in their corrosion resistance with coating thickness as variables. Corrosion potential was measured and analyzed corresponding to the microstructure of the coatings. Keywords: High Heat Resistant Coatings, Gas Tunnel Type Plasma Spraying, Hardness,

Structure and Properties of Thermal Barrier Coating Prepared by Alumina Coated Zirconia Composite Powder

The Microstructure of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

Preparation and Properties of Thermal Barrier Coating with Nanometer Alumina Coated Zirconia

Thermal Insulation Property of Nanostructured Alumina Coated Zirconia Thermal Barrier Coating

Bonding Strength and Thermal Insulation Property of Thermal Barrier Coating with Nanometer Alumina Coated Zirconia

Microstructure and thermal behaviour of plasma sprayed zirconia/alumina composite coating

Microstructure and properties of Al2O3-ZrO2-Y2O3 coatings during high temperature and thermal shock resistance

Preparation of Al 2 O 3 –zro 2 –Y 2 O 3 Composite Coatings by a Modified Sol–Gel Technique for Thermal Barrier Application

Microstructure and properties of Al2O3–ZrO2–TiO2 composite coatings prepared by plasma spraying

Formation of high heat resistant coatings by using gas tunnel type plasma spraying

Microstructure and properties evolution of plasma sprayed Al2O3-Y2O3 composite coatings during high temperature and thermal shock treatment

Effect of spraying ceramic powder pore structure on thermophysical properties of plasma-sprayed thermal barrier coatings

Microstructural Characterization and Thermal Barrier Effects of Conventional and Nanostructured Zro2-7wt.%Y2o3 Thermal Barrier Coatings Deposited by Plasma Spraying

Preparation and Flame Ablation Resistance of Al/Zn/Cu-Incorporated Yttria Partially Stabilized Zirconia Coating

Superior toughness of thermal barrier coating caused by co-doping of trivalent and pentavalent oxides

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

Thickness effect of an alumina–zirconia–mullite composite coating on the properties of zirconia

Core-shell Structured YSZ/CeO 2 Composite Thermal Barrier Coating Fabrication and Properties

Thermophysical properties and cyclic lifetime of plasma sprayed SrAl 12 O 19 for thermal barrier coating applications

Microstructure and Thermophysical Properties of SrZrO3 Thermal Barrier Coating Prepared by Solution Precursor Plasma Spray

Deposition Characteristics, Sintering and Cmas Corrosion Resistance, and Mechanical Properties of Thermal Barrier Coatings by Atmospheric Plasma Spraying