Abstract:The work aims to explore effects of citric acid concentration, sodium tungstate concentration in sulphate bath as well as plating heat treatment process on tungsten content in nickel tungsten alloy plating, plating hardness, plating microstruc-ture and phase composition. Ni-W alloy platings of certain thickness were prepared different bath composition on low carbon steel in alloy electrodeposition method. Later the platings were treated in different heat treatment processes. Microstructure of the platings was observed with scanning electron microscopy (SEM) , and tungsten content of the plating was detected by its built-in EDS energy spectrum. Phase composition, grain size and lattice distortion of the platings were analyzed by X-ray dif-fractometer (XRD). Hardness of the alloy platings was tested with micro hardness tester. With the increase of sodium tungstate concentration or decrease of citric acid concentration in the bath, tungsten content in the plating increased, grain size decreased and Vickers hardness increased. Heat treatment atmosphere had little effect on hardness of the platings, but it could change mi-crostructure of the platings, hardness of the platings first increased and then decreased with the increase of heat treatment tem-perature and holding time. When the bath contains 45 g/L sodium tungstate and 45 g/L citric acid, the obtained plating is substi- tutional sosoloid Ni17W3 with Ni as solvent and W as solute. In this process, the plating is smooth and crack-free, and hardness of the plating is 894 HV0.1 after later heat treatment for 1.5 h under the protection of argon at 400℃ .

High Hardness and Wear Resistance Electroless Ni-P Deposits Without Heat Treatment

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Improved microhardness and wear resistance of the as-deposited electroless Ni–P coating

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

CHEMICAL PLATING MECHANISM IN ACID BATHS AND FABRICATION OF Ni-P COATING WITH HIGH P CONTENT

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Exploring the dual effect of sodium lignosulfonate-modified LDH treatment and heat processing on elevating corrosion and wear resistance of Ni-W composite coatings

Deposition Mechanism and Wear Resistance Nano Ni-Al2O3 Composite Coatings

Electrodeposition of Ni-W Alloy in Sulphate System

Optimization of the Electroplating Process for Amorphous Nickel- Phosphorus Alloy

Microstructure and wear properties of crystalline W alloy coatings prepared by electrodeposition

Study on Electroless Plating Ni-W-P Ternary Alloy with High Tungsten from Compound Complexant Bath

Electrodeposition of nanocrystalline Ni-W coatings with citric acid system

Wear and Corrosion Properties of Crystalline Ni-W Alloy Coatings Prepared by Electrodeposition

Wear Behavior of Electrodeposited Ni-PFunctionally Gradient Deposits

A novel electrochemical deposited Fe Ni coating designed by laser-induced periodic current density: Effect of microstructure on microhardness and wear resistance improvement

Characteristic and Fabrication of Low Stress Ni-W/Ni Laminated Micro-Mould

Study on Structure and Properties of Electrodeposited Co-Ni Alloy Deposits

Deposition Mechanism and Wear Resistance Nano Ni-Al<sub>2</sub>O<sub>3</sub> Composite Coatings

Mechanical properties of Ni-based coatings fabricated by electroless plating method

Electrodeposition of Ni-W-P alloy