Abstract:Cobalt-phosphorus (Co-P) alloy is a promising material for the replacement of traditional hard chromium alloy of high hardness. In this paper, the cobalt-phosphorus alloy layer with high phosphorus content was formed by electrodeposition in a cobalt sulfate solution system under direct current (DC), single pulse (SP) current and double pulse (DP) current, separately. Surface morphology, structure and properties of the deposited layer were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), differential scanning calorimetry (DSC), Vickers microhardness and a neutral salt spray test, respectively. The results showed that the dense Co-P coatings could be obtained by DC, SP and DP with P content of 9.6, 8.9 and 9.1 wt %, respectively. After 30 min heat treatment at 400 °C, coatings deposited under DC, SP and DP currents transformed from an amorphous to a nanocrystalline state, while the grain size was 12–13 nm, 10–12 nm and 8–10 nm, respectively. Among all these conditions, the microhardness of coatings deposited under DP current was the highest, which was 1211 HV, while the microhardness of coatings deposited under DC current was the lowest but higher than that of hard chromium. The wear rate of Co-P coatings was 4 × 10−6–5 × 10−6 mm3/N m with Si3N4 ball as bearing material, which was lower than that of hard chromium. In coatings deposited under different currents with a thickness of ca. 40 μm, no visible corrosion area appeared after 1000 h of a neutral salt spray test. Coatings heated at 300 and 400 °C reached the corrosion grade 7 and grade 4–5, respectively after 1000 h of a neutral salt spray test, so the wear resistance of Co-P coatings was better than that of hard chromium.

Improved microhardness and wear resistance of the as-deposited electroless Ni–P coating

High Hardness and Wear Resistance Electroless Ni-P Deposits Without Heat Treatment

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Optimization of the Electroplating Process for Amorphous Nickel- Phosphorus Alloy

Effects of NH4F on the deposition rate and buffering capability of electroless Ni–P plating solution

Electrodeposition of Ni-W-P alloy

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Enhancement of Wear and Corrosion Resistance of M2052 Damping Alloys by Electroless Plating Ni–P Coating

A novel electrochemical deposited Fe Ni coating designed by laser-induced periodic current density: Effect of microstructure on microhardness and wear resistance improvement

Ni-P coatings electroplating - A review, Part I: Pure Ni-P alloy

Effect of Waveform and Heat Treatment Processes on the Performance of Electrodeposited Co-P Coating

Study on property of electroless plating Ni-W-P coating

Analysis of P-contents Influence on Ni-p Coating Performance

Effect of Pulse Reverse Electroplating Technology on the Properties of Amorphous Ni-P Alloy Coating

Electrochemical Synthesis and Characterization of Ni–P Alloy Coatings from Eutectic–Based Ionic Liquid

Preparation and Properties of Ni–Co–P/nano‐sized Si3N4 Electroless Composite Coatings

Hardness and tribological properties of co-electrodeposited Ni-W-B/B coatings

Microstructure and wear properties of crystalline W alloy coatings prepared by electrodeposition

Preparation of Amorphous Nickel-Phosphorus Alloy Coating by Electroplating

Microstructure, Friction and Wear Behavior and Corrosion Resistance of electroless Double-Layer Ni-P/Ni-Mo-P Coatings on AZ91D Magnesium Alloy

Strengthening the mechanical properties and corrosion resistance of Ni W coatings by PDA-functionalized h-BN nanosheets