Abstract:The nanostructure‐controllable TaSi2 arrays with vertically aligned nanotips are produced through a novel and straightforward method, involving advanced directional solidification, heat treatment, and etching process. The enhanced sharpness and high regularity of the TaSi2 nanotip array contribute to its favorable field emission performance, thereby advancing the potential application of TaSi2 as a cold cathode material in electronic devices. Recognizing the strong potential of cold cathodes for important commercial applications in fields such as electronics, there is a growing interest in the exploration of novel 1D nanomaterials. Among various cold cathode materials, TaSi2 is of great interest for its outstanding field emission performance. In this work, the Si‐TaSi2 eutectic composite with nano‐sized highly oriented TaSi2 fibers and semi‐coherent phase interfaces is prepared by the laser floating zone melting technique with a very high‐temperature gradient of 6000 K cm−1 at a solidification rate of 200 μm s−1. On the basis of directionally solidified Si‐TaSi2 eutectic composite, well‐aligned TaSi2 nanorod and nanotip arrays are fabricated by inductively coupling plasma (ICP) etching process and HNO3/HF wet etching process, respectively. The field emission measurements show that the field enhancement factor, turn‐on electric field, and effective work function are strongly affected by tip morphologies. The TaSi2 array with regular nanotip structure possesses the best field emission characteristic among all TaSi2 nanostructures, with a relatively low turn‐on field of 4.8 V μm−1 and a high current density of 733 μA cm−2. These findings preliminarily establish a clear relationship between the performance and structure of the array, providing technical guidance for the application of this material in electronic devices.

Field electron emission from ultra-high density Si nanotip arrays

Fabrication and field emission property of a Si nanotip array

Precisely-controlled Fabrication of Single ZnO Nanoemitter Arrays and Their Possible Application in Low Energy Parallel Electron Beam Exposure.

Field Electron Emission of Si Nanotips with Apexes of Various Compositions

Aluminum-enhanced sharpening of silicon nanocones

Field Emission Tip Array Fabrication Utilizing Geometrical Hindrance in the Oxidation of Si

Fabrication and characterization of Si nanotip arrays for Si-based nano-devices

Electron Field Emission Characteristics from Single-crystal Silicon Nanoarrays Fabricated by Direct Lithography with Nanosphere Mask

Fabrication And Field Emission Study Of Atomically Sharp High-Density Tungsten Nanotip Arrays

Insight into TaSi2 Nanostructures with Different Morphologies and Their Field Emission Properties

Laser microstructuring of Si surfaces for low-threshold field-electron emission

Morphology Control and Electron Field Emission Properties of High-Ordered Si Nanoarrays Fabricated by Modified Nanosphere Lithography

Stable Field Emission from Vertically Oriented SiC Nanoarrays

Quasi-Saturated Arsenic Concentration and Uniform Electron Emission by Regulating Thermal Oxidation of Si Nanotips

TiO2 Nanotip Arrays: Anodic Fabrication and Field-Emission Properties

Formation and Field Emission Characteristics of Amorphous and Crystalline Si Nanoarrays

3-D finite element calculation of electric field enhancement for nanostructures fabrication mechanism on silicon surface with AFM tip induced local anodic oxidation

Field-Emission Properties of Nanostructured Wo3 Arrays Fabricated Using Tungsten Hot-Filament Chemical Vapor Deposition

Silicon Tip Arrays with Ultrathin Amorphous Diamond Apexes

Si-Tips with Saturated High Concentration Arsenic Dopant at the Nano-Apexes for Uniform Field Electron Emission

Enhancing Electron Emission From Silicon Tip Arrays By Using Thin Amorphous Diamond Coating