Abstract:Films are deposited from a single Al(20)Cr(20)Mo(20)Si(21)Ti(19) alloy target in various argon/nitrogen atmospheres by direct current magnetron sputtering. Two sets of substrate parameters are examined; one with a substrate temperature of 300 K and the substrate grounded (U(0) (V,) (300 K)), and the other with the substrate biased at -50 V and its temperature maintained at 573 K (U(-50 V, 573 K)). The films produced in pure argon or at lower nitrogen flow rates are amorphous, regardless of the substrate parameters. At higher nitrogen flow rates, however, all of the coatings are found to form an FCC (face-center-cubic) NaCl-type structure. Although this coating system contains several well known immiscible nitrides, i.e. TiN, AN and Si(3)N(4), it is determined that only a single FCC phase forms, namely a single FCC (AlCrMoSiTi)N solid solution, regardless of the deposition conditions. The lower deposition rate and reduced surface roughness of the U(-50 V, 573 K) films compared to the UO V, 300 K films are considered to result from the increased densification and resputtering of coating material. The majority of the coatings are found to have hardnesses of only 10 to 16 GPa. The highest hardnesses of 25 and 22 GPa are obtained for the crystalline nitride U(-50 V, 573 K) coatings deposited at N(2)/(Ar+N(2)) ratios of 50 and 67%, respectively. More in depth explanations behind the structure and properties of these multi-element films are presented within the paper. (c) 2008 Elsevier B.V. All rights reserved.

Effects of Substrate Temperature and Post-Annealing on Microstructure and Properties of (alcrnbsitiv)n Coatings

Effects of Substrate Bias on Structure and Mechanical Properties of (alcrnbsitiv)n Coatings

Effects of annealing temperature on the microstructure, mechanical and tribological properties of CrAlTiN coatings

Influence of substrate bias, deposition temperature and post-deposition annealing on the structure and properties of multi-principal-component (AlCrMoSiTi)N coatings

Mechanical and Tribological Properties of Multi-Element (alcrtatizr)n Coatings

Influence Of Annealing Temperature On Film Morphology And Tribological Performance Of Tisin-Ag Coating

Structure and Properties of Two Al–Cr–Nb–Si–Ti High-Entropy Nitride Coatings

Post-deposition annealing effects on microstructure, mechanical and tribological properties of AlCrN films

Effects of nitrogen content on structure and mechanical properties of multi-element (AlCrNbSiTiV)N coating

Inhibition of grain coarsening up to 1000°C in (AlCrNbSiTiV)N superhard coatings

Structural and Mechanical Properties of Multi-Element (alcrmotatizr)nx Coatings by Reactive Magnetron Sputtering

Effects of Heat Treatment on Structure Transformation of Cr/Al Composite Coatings

Effect of the Post-Deposition Thermal Treatment on the Mechanical Properties of a Compositionally Modulated CrAlSiN-AlSiN Coating

Nitride Films Deposited from an Equimolar Al–Cr–Mo–Si–Ti Alloy Target by Reactive Direct Current Magnetron Sputtering

Influence of annealing on microstructures and mechanical properties of arc-deposited AlCrTiSiN coating

Effect of annealing on the microstructure, mechanical and electrochemical properties of CrAlC coatings

Effects of substrate bias on the structure and mechanical properties of (Al 1.5 CrNb 0.5 Si 0.5 Ti)N x coatings

Annealing Effect On The Microstructure Modification And Tribological Properties Of Amorphous Carbon Nitride Films

Strong Amorphization of High-Entropy AlBCrSiTi Nitride Film

Mechanical Properties of the TiAlSiN Coatings by Post Heat Treatments

Effects of Nitrogen Flow Ratio on the Structure and Properties of Reactively Sputtered (almonbsitativzr)n(x) Coatings