Abstract:Precursor infiltration and pyrolysis (PIP) and chemical vapor infiltration (CVI) were used to fabricate SiC/SiC composites on a four-step 3D SiC fibre preform deposited with a pyrolytic carbon interface. The effects of fabrication processes on the microstructure and mechanical properties of the SiC/SiC composites were studied. Results showed the presence of irregular cracks in the matrix of the SiC/SiC composites prepared through PIP, and the crystal structure was amorphous. The room temperature flexural strength and modulus were 873.62 MPa and 98.16 GPa, respectively. The matrix of the SiC/SiC composites prepared through CVI was tightly bonded without cracks, the crystal structure had high crystallinity, and the room temperature bending strength and modulus were 790.79 MPa and 150.32 GPa, respectively. After heat treatment at 1300 degrees C for 50 h, the flexural strength and modulus retention rate of the SiC/SiC composites prepared through PIP were 50.01% and 61.87%, and those of the composites prepared through CVI were 99.24% and 96.18%, respectively. The mechanism of the evolution of the mechanical properties after heat treatment was examined, and the analysis revealed that it was caused by the different fabrication processes of the SiC matrix. After heat treatment, the SiC crystallites prepared through PIP greatly increased, and the SiOxCy in the matrix decomposed to produce volatile gases SiO and/or CO, ultimately leading to an increase in the number of cracks and porosity in the material and a decrease in the material load-bearing capacity. However, the size of the SiC crystallites prepared through CVI hardly changed, the SiC matrix was tightly bonded without cracks, and the load-bearing capacity only slightly changed.

Processing and Properties of 2D SiC/SiC Composites by Precursor Infiltration and Pyrolysis

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

Mechanical properties and oxidation resistance of SiC f/CVI-SiC composites with PIP-SiC interphase

MECHANICAL PROPERTY OF 2.5 DIMENSIONAL SILICON CARBIDE FIBER REINFORCED SILICON CARBIDE COMPOSITES

Fabrication and characterization of 2.5D and 3D SiCf/SiC composites

Mechanical and dielectric properties of 2.5D SiCf/SiC-Al2O3 composites prepared via precursor infiltration and pyrolysis

High Performance SiC/SiOC Composites with in Situ Carbon Interface

The Fabrication of 2D Cf/SiC Composite by a Modified PIP Process Using Active Al Powders As Active Filler

The Effect of the Pyc Interphase Coating on the Microwave Heating Sintered Sic/Sic Composites

Mechanical and Dielectric Properties of SiC F /sic Composites Fabricated by PIP Combined with CIP Process

Mechanical Properties of SiC/SiC Composites by PIP Process with a New Precursor at Elevated Temperature

Mechanical Properties of SiCf/SiC Composites with PyC and the BN Interface

High-performance 3D SiC/PyC/SiC Composites Fabricated by an Optimized PIP Process with a New Precursor and a Thermal Molding Method

2.5-DIMENSION SiCf/SiC COMPOSITES FABRICATED BY LOW PRESSURE CHEMICAL VAPOR INFILTRATION

Influence of polycarbosilane composition on the properties of SiC/SiC composite fabricated by precursor infiltration and pyrolysis process

The Effect of PyC/SiC Compound Interphase on the Properties of PIP SiC/SiC Composite

Mechanical Property And Toughening Mechanism Of 2.5d C/C-Sic Composites With High Textured Pyrocarbon Interface

Effects of fabrication processes on the properties of SiC/SiC composites