Abstract:Precursor infiltration and pyrolysis (PIP) and chemical vapor infiltration (CVI) were used to fabricate SiC/SiC composites on a four-step 3D SiC fibre preform deposited with a pyrolytic carbon interface. The effects of fabrication processes on the microstructure and mechanical properties of the SiC/SiC composites were studied. Results showed the presence of irregular cracks in the matrix of the SiC/SiC composites prepared through PIP, and the crystal structure was amorphous. The room temperature flexural strength and modulus were 873.62 MPa and 98.16 GPa, respectively. The matrix of the SiC/SiC composites prepared through CVI was tightly bonded without cracks, the crystal structure had high crystallinity, and the room temperature bending strength and modulus were 790.79 MPa and 150.32 GPa, respectively. After heat treatment at 1300 degrees C for 50 h, the flexural strength and modulus retention rate of the SiC/SiC composites prepared through PIP were 50.01% and 61.87%, and those of the composites prepared through CVI were 99.24% and 96.18%, respectively. The mechanism of the evolution of the mechanical properties after heat treatment was examined, and the analysis revealed that it was caused by the different fabrication processes of the SiC matrix. After heat treatment, the SiC crystallites prepared through PIP greatly increased, and the SiOxCy in the matrix decomposed to produce volatile gases SiO and/or CO, ultimately leading to an increase in the number of cracks and porosity in the material and a decrease in the material load-bearing capacity. However, the size of the SiC crystallites prepared through CVI hardly changed, the SiC matrix was tightly bonded without cracks, and the load-bearing capacity only slightly changed.

Effects of fabrication processes on the properties of SiC/SiC composites

Effect of Pyrolysis Temperature on the Mechanical Evolution of SiCf/SiC Composites Fabricated by PIP

Effect of High-Temperature Heat Treatment on the Microstructure and Mechanical Behavior of PIP-based C/C-SiC Composites with SiC Filler

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Cf/Sic Composites

Microstructure and flexural properties of C/SiC composites by CVI-RMI method

Effects of CVI SiC amount and deposition rates on properties of SiCf/SiC composites fabricated by hybrid chemical vapor infiltration (CVI) and precursor infiltration and pyrolysis (PIP) routes

Fabrication of Cf/SiC composites by precursor infiltration and pyrolysis process

Mechanical Properties of SiC/SiC Composites by PIP Process with a New Precursor at Elevated Temperature

Influences of Thermal Molding Process on the Flexural Properties of SiC/SiC Composites with a New Precursor Polymer

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

Tensile Behaviors and Matrix Cracking Mechanism of C/SiCN Composite Prepared by Precursor Infiltration Pyrolysis Method

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

Effect of heat treatment on microstructure and mechanical properties of PIP-SiC/SiC composites

Effect of PIP Process on Microstructure and Mechanical Properties of 2D C/SiC-ZrB_2 Composites

High-performance 3D SiC/PyC/SiC Composites Fabricated by an Optimized PIP Process with a New Precursor and a Thermal Molding Method

The effects of preparation temperature on the SiCf/SiC 3D4d woven composite

The Effect of Heat Treatment on the Properties of SiCf/SiC Composites Prepared with Different SiC Fibers

Effect of Fabrication Process of Carbon Interlayer on Mechanical Properties of SiC_f/SiC Composites

The Effect of PyC/SiC Compound Interphase on the Properties of PIP SiC/SiC Composite

MECHANICAL PROPERTY OF 2.5 DIMENSIONAL SILICON CARBIDE FIBER REINFORCED SILICON CARBIDE COMPOSITES