Abstract:Unidirectional (UD) SiCf/SiC composites were prepared using chemical vapor infiltration (CVI)-polymer infiltration and pyrolysis (PIP) hybrid procedure at different PIP temperatures of 1100 degrees C (1100PIP), 1300 degrees C (1300PIP), and 1500 degrees C (1500PIP). The effect of PIP temperature on the microstructure of each component was studied. Results showed that SiC fiber strength and interfacial shear strength (IFSS) were the main factors affecting the mechanical properties of the composite. At 1100 degrees C, the fiber was thermally stable and IFSS was high, due to which 1100PIP achieved ultrahigh mechanical performance with tensile strength of 901.0 f 87.7 MPa, flexural strength of 2186.5 f 192.5 MPa, and toughness of 80.6 f 12.0 MPa center dot m1/2. At 1300 degrees C, IFSS decreased slightly, due to the crystallization of BN interphase. Hence, the mechanical performance of 1300PIP decreased slightly to 789.8 f 42.9 MPa, 1935.9 f 163.2 MPa, and 58.2 f 4.0 MPa center dot m1/2, respectively. At 1500 degrees C, severe fiber ceramization and decrease in IFSS caused severe decline in mechanical performance to about half of that of 1100PIP. The crack could be deflected not only at the fiber/BN (F/B) interface, but also at the CVI SiC/PIP SiC (C/P) interface, due to the existence of free carbon layers at the C/P interface, which played an important role in improving the strength and toughness of the composite. 1300PIP also showed excellent strength at high - temperature. At 1350 degrees C and 1500 degrees C, its flexural strengths were as high as 1529.0 f 73.0 MPa and 1223.1 f 81.1 MPa, respectively. The thermal conductivity and thermal expansion coefficient were also tested. Their values were mainly affected by the grain size and thermal stabilities of the SiC fiber and PIP matrix.

Mechanical Properties of SiC/SiC Composites by PIP Process with a New Precursor at Elevated Temperature

High-temperature Mechanical Properties of Thermal Barrier Coated SiC/SiC Composites by PIP Process with a New Precursor Polymer

High-performance 3D SiC/PyC/SiC Composites Fabricated by an Optimized PIP Process with a New Precursor and a Thermal Molding Method

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

High-Temperature Flexural Properties of SiC/SiC Composites With a New Precursor Polymer

Fabrication of SiC/SiC Composites by Improved PIP Processing with a New Precursor Polymers

Fabrication of Cf/SiC composites by precursor infiltration and pyrolysis process

Influences of Thermal Molding Process on the Flexural Properties of SiC/SiC Composites with a New Precursor Polymer

Processing and mechanical performance of 3D Cf/SiCN composites prepared by polymer impregnation and pyrolysis

Effects of fabrication processes on the properties of SiC/SiC composites

Processing and Properties of 2D SiC/SiC Composites by Precursor Infiltration and Pyrolysis

Mechanical, Oxidation and Ablation Properties of C/(C-SiC)CVI-(ZrC-SiC)PIP Composites

Mechanical and Dielectric Properties of SiC F /sic Composites Fabricated by PIP Combined with CIP Process

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

Ultrahigh Room and High - Temperature Mechanical Properties of SiCf/SiC Composites Prepared by Hybrid CVI and PIP Methods: Effects of PIP Temperature

Effect of Pyrolysis Temperature on the Mechanical Evolution of SiCf/SiC Composites Fabricated by PIP

C/C–SiC Composites Derived from Single‐source Poly(silylene–acetylene) Precursors

Microstructure and Properties of SiCw/SiC Composites Prepared by Gel-Casting Combined with Precursor Infiltration and Pyrolysis

Mechanical properties and high temperature failure mechanism of carbon fibers reinforced polysilazane-derived SiCN ceramic matrix composites via PIP process

Effects of pyrolysis temperatures on the oxidation behavior of PIP-processed SiCf/SiC composites

Property Evolvements in SiCf/SiC Composites Fabricated by Combination of PIP and Electrophoretic Deposition at Different Pyrolysis Temperatures