Abstract:Precursor infiltration and pyrolysis (PIP) and chemical vapor infiltration (CVI) were used to fabricate SiC/SiC composites on a four-step 3D SiC fibre preform deposited with a pyrolytic carbon interface. The effects of fabrication processes on the microstructure and mechanical properties of the SiC/SiC composites were studied. Results showed the presence of irregular cracks in the matrix of the SiC/SiC composites prepared through PIP, and the crystal structure was amorphous. The room temperature flexural strength and modulus were 873.62 MPa and 98.16 GPa, respectively. The matrix of the SiC/SiC composites prepared through CVI was tightly bonded without cracks, the crystal structure had high crystallinity, and the room temperature bending strength and modulus were 790.79 MPa and 150.32 GPa, respectively. After heat treatment at 1300 degrees C for 50 h, the flexural strength and modulus retention rate of the SiC/SiC composites prepared through PIP were 50.01% and 61.87%, and those of the composites prepared through CVI were 99.24% and 96.18%, respectively. The mechanism of the evolution of the mechanical properties after heat treatment was examined, and the analysis revealed that it was caused by the different fabrication processes of the SiC matrix. After heat treatment, the SiC crystallites prepared through PIP greatly increased, and the SiOxCy in the matrix decomposed to produce volatile gases SiO and/or CO, ultimately leading to an increase in the number of cracks and porosity in the material and a decrease in the material load-bearing capacity. However, the size of the SiC crystallites prepared through CVI hardly changed, the SiC matrix was tightly bonded without cracks, and the load-bearing capacity only slightly changed.

High-performance 3D SiC/PyC/SiC Composites Fabricated by an Optimized PIP Process with a New Precursor and a Thermal Molding Method

Mechanical Properties of SiC/SiC Composites by PIP Process with a New Precursor at Elevated Temperature

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

Fabrication of SiC/SiC Composites by Improved PIP Processing with a New Precursor Polymers

Influences of Thermal Molding Process on the Flexural Properties of SiC/SiC Composites with a New Precursor Polymer

High-temperature Mechanical Properties of Thermal Barrier Coated SiC/SiC Composites by PIP Process with a New Precursor Polymer

Processing and mechanical performance of 3D Cf/SiCN composites prepared by polymer impregnation and pyrolysis

High-Temperature Flexural Properties of SiC/SiC Composites With a New Precursor Polymer

Low-cost C/SiC Composites Prepared by CVI+Pressure-PIP Hybrid Process

High Performance SiC/SiOC Composites with in Situ Carbon Interface

Mechanical and Dielectric Properties of SiC F /sic Composites Fabricated by PIP Combined with CIP Process

Fabrication of Cf/SiC composites by precursor infiltration and pyrolysis process

Effects of In-Situ Carbon Layer and Volume Fraction of SiC Fiber on the Mechanical Properties and Fracture Behaviors of SiCf/SiC Composites Fabricated by a Modified PIP Method

Fabrication and characterization of 2.5D and 3D SiCf/SiC composites

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

High Performance Csf/SiC Ceramic Matrix Composites Fabricated by Material Extrusion 3D Printing and Precursor Infiltration and Pyrolysis

Effect of polymer infiltration and pyrolysis (PIP) on microstructure and properties of high volume fraction SiC/Al composites prepared by a novel hybrid additive manufacturing

Effects of fabrication processes on the properties of SiC/SiC composites

Microstructure and Properties of SiCw/SiC Composites Prepared by Gel-Casting Combined with Precursor Infiltration and Pyrolysis

Building SiC-based composites from polycarbosilane-derived 3D-SiC scaffolds via polymer impregnation and pyrolysis (PIP)

The Fabrication of 2D Cf/SiC Composite by a Modified PIP Process Using Active Al Powders As Active Filler