Abstract:Precursor infiltration and pyrolysis (PIP) and chemical vapor infiltration (CVI) were used to fabricate SiC/SiC composites on a four-step 3D SiC fibre preform deposited with a pyrolytic carbon interface. The effects of fabrication processes on the microstructure and mechanical properties of the SiC/SiC composites were studied. Results showed the presence of irregular cracks in the matrix of the SiC/SiC composites prepared through PIP, and the crystal structure was amorphous. The room temperature flexural strength and modulus were 873.62 MPa and 98.16 GPa, respectively. The matrix of the SiC/SiC composites prepared through CVI was tightly bonded without cracks, the crystal structure had high crystallinity, and the room temperature bending strength and modulus were 790.79 MPa and 150.32 GPa, respectively. After heat treatment at 1300 degrees C for 50 h, the flexural strength and modulus retention rate of the SiC/SiC composites prepared through PIP were 50.01% and 61.87%, and those of the composites prepared through CVI were 99.24% and 96.18%, respectively. The mechanism of the evolution of the mechanical properties after heat treatment was examined, and the analysis revealed that it was caused by the different fabrication processes of the SiC matrix. After heat treatment, the SiC crystallites prepared through PIP greatly increased, and the SiOxCy in the matrix decomposed to produce volatile gases SiO and/or CO, ultimately leading to an increase in the number of cracks and porosity in the material and a decrease in the material load-bearing capacity. However, the size of the SiC crystallites prepared through CVI hardly changed, the SiC matrix was tightly bonded without cracks, and the load-bearing capacity only slightly changed.

MECHANICAL PROPERTY OF 2.5 DIMENSIONAL SILICON CARBIDE FIBER REINFORCED SILICON CARBIDE COMPOSITES

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

2.5-DIMENSION SiCf/SiC COMPOSITES FABRICATED BY LOW PRESSURE CHEMICAL VAPOR INFILTRATION

Fabrication of SiCf/SiO2 Composites and the Influence of Interfaces on the Mechanical Properties

Effect of Fabrication Process of Carbon Interlayer on Mechanical Properties of SiC_f/SiC Composites

Processing and Properties of 2D SiC/SiC Composites by Precursor Infiltration and Pyrolysis

Mechanical Property And Toughening Mechanism Of 2.5d C/C-Sic Composites With High Textured Pyrocarbon Interface

Microstructure and Mechanical Properties of SiCf/SiC Composite Prepared by Chemical Vapor Infiltration

Microstructure and Mechanical Properties of Three-Dimensional Carbon/Silicon Carbide Composites Fabricated by Chemical Vapor Infiltration

Mechanical Properties of SiCf/SiC Composites with PyC and the BN Interface

Microstructure, Interfacial and Mechanical Properties of SiC Interphase Modified C/C-SiC Composites Prepared by Reactive Melt Infiltration

Preparation and Properties of Continuous Carbon Fiber-Reinforced Silicon Carbide Composites

Microstructure and mechanical properties of SiC f /SiC composite prepared by chemical vapor infiltration

Study of Properties of Silicon Carbide Fiber Reinfoced Si-O-C Composites Using Low Cost Polysiloxane

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

Effects of fabrication processes on the properties of SiC/SiC composites

Effect of Pyc Interphase Thickness on Mechanical Behaviors of Sibc Matrix Modified C/Sic Composites Fabricated by Reactive Melt Infiltration

Effect of Pyrocarbon Content in C/C Preforms on Microstructure and Mechanical Properties of the C/C–SiC Composites

Mechanical Properties and Failure Behavior of 3D-SiCf/SiC Composites with Different Interphases