Abstract:Significant matrix cracks and residual pores may form within ceramic matrix composite which was prepared by polymer infiltration and pyrolysis (PIP) method. Explore the matrix cracking mechanism and the crack evolution behavior would benefit the design and performance optimization of the composite. A spinning PIP process in vacuum was adopted to prepare mini C/SiCN composite without weak interphase. The tensile properties and the matrix crack evolution phenomena were analyzed. The influences of PIP cycles and heat-treatment temperatures were discussed. Results showed that the compositions are essentially the same for the samples heat-treated at 1000-1400 V. While the heat-treatment temperature rises to 1600 V, the precursor-derived SiCN matrix decomposes, with the carbon content decreased and SiC content increased significantly. As PIP cycles increased from 1 to 4, the average tensile strength of the composite increased by 14.19%, 38.83%, and 63.47%, respectively. The matrix crack spacing and crack opening distance gradually decreased, and the bonding between matrix and fiber was enhanced, leading to little fiber pull-out. When the heat-treatment temperature increased from 1000 degrees C to 1400 degrees C, the tensile strength of the composite changed slightly. In contrast, when heat-treatment temperature roses to 1600 degrees C, the SiCN matrix was transformed from amorphous SiCxN4-x tetrahedron structural units to SiC crystals. Then the matrix and the fiber debonded, resulting in their bonding strength weakened. As a result, the tensile strength of the C/SiCN composite decreased by 30.0%, due to a combined effect of interfacial debonding and fiber damage.

Tensile Behaviors and Matrix Cracking Mechanism of C/SiCN Composite Prepared by Precursor Infiltration Pyrolysis Method

Properties of Carbon Nano-Tubes–cf/sic Composite by Precursor Infiltration and Pyrolysis Process

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Processing and mechanical performance of 3D Cf/SiCN composites prepared by polymer impregnation and pyrolysis

Mechanical properties and high temperature failure mechanism of carbon fibers reinforced polysilazane-derived SiCN ceramic matrix composites via PIP process

Residual stress and interface debonding behavior in Si3N4w reinforced SiCN composites prepared by the PIP process: A case study

Microstructure and mechanical properties of 3D Cf/SiBCN composites fabricated by polymer infiltration and pyrolysis

Effects of CVI SiC amount and deposition rates on properties of SiCf/SiC composites fabricated by hybrid chemical vapor infiltration (CVI) and precursor infiltration and pyrolysis (PIP) routes

C/C–SiC Composites Derived from Single‐source Poly(silylene–acetylene) Precursors

In-situ Tensile Damage and Fracture Behavior of PIP SiC/SiC Minicomposites at Room Temperature

Mechanical /thermal Shock Properties and Failure Mechanisms of Cf/SiBCN Composites Effect of Sintering Densification and Fiber Coating

Preparation of SiC fiber-reinforced SiC composites

Fatigue behavior and damage analysis of PIP C/SiC composite

The Effect of PyC/SiC Compound Interphase on the Properties of PIP SiC/SiC Composite

Rapid Fabrication of C/C/SiC Composite by PIP of HMDS

Effect of pyrocarbon interphase texture and thickness on tensile damage and fracture in T‐700TM carbon fiber–reinforced silicon carbide minicomposites

Effect of Pyrocarbon Content in C/C Preforms on Microstructure and Mechanical Properties of the C/C–SiC Composites

Multiscale study of the process deformation for SiC/SiC composite materials in PIP process

PyC interphase growth mechanism and control models of C/SiC composites

Microstructure and Mechanical Properties of C/C Composites Modified by Single-Source Precursor Derived Ceramics