Abstract:SiC fiber-reinforced SiC matrix (SiCf/SiC) composites are promising materials for high-temperature structural applications. In this study, KD-II SiC fiber bundles with a C/Si ratio of approximately 1.25 and an oxygen amount of 2.53%, were used as reinforcement. PyC interphase, PyC-SiC co-deposition interphase I and II, with different thicknesses, and SiC matrix were deposited into the SiC fiber bundles by using chemical vapor infiltration (CVI) to form SiCf/SiC mini composites. When the thickness of the interphase is approximately 1000 nm, the ultimate tensile stress and strain of SiCf/SiC mini composites with PyC-SiC co-deposition interphase I can reach 1120.0 MPa and 0.72%, respectively, which are significantly higher than those of SiCf/SiC mini composites with a PyC interphase (740.0 MPa, 0.87%) and PyC-SiC co-deposition interphase II (645.0 MPa, 0.54%). The effect of thicknesses and types of interphase on tensile fracture behavior of mini composites and then the fracture mechanism are discussed in detail.
What problem does this paper attempt to address?
The problem this paper attempts to address is the study of the effects of different types and thicknesses of interphases on the tensile properties of silicon carbide fiber-reinforced silicon carbide matrix composites (SiC f/SiC mini composites). Specifically, the authors aim to optimize the mechanical properties of the composites, particularly improving their tensile strength and strain capacity, by introducing different types of interphases (such as PyC, PyC-SiC co-deposited interphases, etc.) and adjusting the thickness of the interphases.
### Main Research Content:
1. **Preparation Method**: Using chemical vapor infiltration (CVI) technology to deposit different types of interphases (PyC, PyC-SiC co-deposited interphases I and II) and SiC matrix within SiC fiber bundles to form SiC f/SiC mini composites.
2. **Performance Testing**: Testing the mechanical properties of the composites through tensile tests, including tensile strength and strain, and analyzing the effects of different interphase types and thicknesses on these properties.
3. **Microstructure Characterization**: Using scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM) to observe the microstructure and fracture morphology of the composites, exploring the distribution of interphases and their impact on the composite properties.
4. **Fracture Mechanism Analysis**: Investigating the effects of different interphase types and thicknesses on crack propagation behavior by analyzing the fracture morphology of the composites, thereby revealing the fracture mechanisms of the composites.
### Research Background:
- SiC f/SiC composites have broad application prospects in aerospace, nuclear energy, and other fields due to their low density, high strength, high modulus, excellent high-temperature oxidation resistance, and erosion resistance.
- The interphase is one of the key factors affecting the mechanical properties of SiC f/SiC composites. Although traditional PyC interphases can improve the performance of composites, their stability in high-temperature oxidation environments is relatively poor. Therefore, developing new interphases to further optimize the performance of composites is of great significance.
### Research Significance:
- By systematically studying the effects of different interphase types and thicknesses on the tensile properties of SiC f/SiC mini composites, this research provides theoretical basis and technical support for optimizing the design and preparation of composites.
- It contributes to the development of high-performance SiC f/SiC composites, promoting their practical application in high-temperature structural applications, especially in the field of nuclear fuel cladding materials.