Abstract:High-textured pyrolytic carbon (PyC) is the ideal interface for SiC fiber-reinforced SiC matrix (SiCf/SiC) composites. To prepare high-textured PyC coatings on SiC fibers efficiently, chemical vapor deposition (CVD) technique was applied with the single precursor ethanol. The effects of CVD parameters on the morphology and textures of PyC were investigated in detail. Rough laminar (RL), smooth laminar (SL) and regenerative laminar (ReL) PyC could be obtained by controlling the CVD parameters. High-textured RL PyC could be stably synthesized in a large distance range in the horizontal tube furnace at 1150 °C and 10–20 kPa (total pressure), which inferred that low temperature and negative pressure were beneficial to the formation of RL PyC. Conversely, when the temperature was up to 1350 °C, the textures of PyC at different deposition positions varied considerably. In the vicinity of isothermal zone, the texture evolution of PyC with deposition positions followed the pattern of SL→RL→SL, which could be ascribed to the ratio change of the small linear hydrocarbons (fillers) and the aromatic hydrocarbons (particles) in the gas phase. The texture evolution followed the Particle-Filler model. In addition to PyC textures, the PyC coating thickness played a critical role in regulating the mechanical properties of SiC fibers and SiCf/SiC composites. In the present work, the effects of thickness of RL PyC coatings on the tensile properties of SiC fibers were investigated. The SiC fibers with 0.3 μm RL PyC coating showed the highest average tensile strength (2735 MPa) and Weilbull modulus (10.34), which might be ascribed to the repair of fiber surface defects and the appropriate stress state between fibers and coatings. The results could provide essential data for the interface design and optimization of SiCf/SiC composites.

Effect of pyrolytic carbon interphase on mechanical properties of mini T800-C/SiC composites

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Properties of Carbon Nano-Tubes–cf/sic Composite by Precursor Infiltration and Pyrolysis Process

Effect of pyrocarbon interphase texture and thickness on tensile damage and fracture in T‐700TM carbon fiber–reinforced silicon carbide minicomposites

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

PyC interphase growth mechanism and control models of C/SiC composites

Preparation and tensile behavior of SiCf/SiC mini composites containing different types and thicknesses of interphase

Influence of thickness of pyrolytic carbon interphase on the mechanical behavior of SiC/(BN/PyC)/SiC composites

The Effect of PyC/SiC Compound Interphase on the Properties of PIP SiC/SiC Composite

Effects of single-phase and Co-deposited interphases on mechanical hysteresis behavior in T700 TM mini-C f /SiC composites

Influence of pyrolytic carbon interphase and pyrolysis temperature on the mechanical and tribological properties of Cf/SiC after heat treatment at 1800 °C

Effects of pyrochemical treatment for producing interfacial carbon layer on tensile properties of polymer-derived-matrix-based SiC/SiC composites

Enhanced thermal and mechanical properties of optimized S i C f / S i C composites with in-situ CNTs on PyC interface

Effects of interphases on thermal expansion of 3D-C/SIC composites

Mechanical properties and strengthening mechanism of SiCf/SiC mini-composites modified by SiC nanowires

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

Texture control of pyrolytic carbon coatings and effects of coating thickness on the tensile properties of SiC fibers

Effects of Interphase Thickness on Damping Behavior of 2D C/SiC Composites

Effects of PyC coating on SiC fibers after ultra-high temperature annealing

Effect of PyC/BN interfacial phases on mechanical behavior of SiC/SiC composites