Abstract:SiCf/SiC composite materials had become a research hotspot in the fields of aerospace materials and nuclear materials in recent years. This materials have high strength, radiation resistance, high temperature resistance and oxidation resistance. However, SiC is a typical brittle material prone to being damaged due to stress concentration in some cases, leading to cracks and even component failure. Therefore, this study employed an accurate and efficient numerical simulation method, phase field cohesive zone method (PFCZM), to investigate the microscopic damage behavior of SiCf/SiC composite materials. This study aimed to illustrate the influence of the thickness of pyrolytic carbon (PyC) interface layer on the failure behavior of SiCf/SiC composite materials. Firstly, this study conducted relevant verification of PFCZM. Secondly, numerical simulations of crack initiation, crack propagation, and final damage were performed by establishing a representative volume element (RVE). Observing the simulation results, it was noted that at low strain, when PyC was thicker, the SiCf/SiC composite materials exhibited slight damage to both the SiC matrix and PyC interface. Conversely, when PyC was thinner, the SiCf/SiC composite materials displayed only slight damage to PyC interface. As the PyC thickness increases, the damage to PyC interface decreases, while the damage to SiC becomes more prominent. Simultaneously, a competitive relationship in the damage behavior of SiCf/SiC composite materials can be found after the SiC matrix has cracked: When PyC is thinner, the damage primarily manifests as interlayer delamination between the SiC matrix and the SiC fiber. Conversely, when PyC is thicker, it manifests in PyC failure. Finally, this study concluded that, in this investigation, a PyC interface layer with a thickness of 0.1 μm exhibited the most effective protective effect on SiCf/SiC composite material.

Influence of thickness of pyrolytic carbon interphase on the mechanical behavior of SiC/(BN/PyC)/SiC composites

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Effect of PyC/BN interfacial phases on mechanical behavior of SiC/SiC composites

Mechanical Properties and Failure Behavior of 3D-SiCf/SiC Composites with Different Interphases

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

Effects of interphases on thermal expansion of 3D-C/SIC composites

The Effect of PyC/SiC Compound Interphase on the Properties of PIP SiC/SiC Composite

Effect of BN interfacial layer on the mechanical behavior of SiC fiber reinforced SiC ceramic matrix composites

Investigation on crack propagation of SiCf/SiC composite via PF-CZM method

Effect of pyrolytic carbon interphase on mechanical properties of mini T800-C/SiC composites

Effect of pyrocarbon interphase texture and thickness on tensile damage and fracture in T‐700TM carbon fiber–reinforced silicon carbide minicomposites

Quantitative In-Situ Study of Strength-Governed Interfacial Failure Between H-Bn and Polymer-Derived Ceramic

Molecular dynamics simulation on PyC interfacial failure mechanism and shear strength of SiC/SiC composites

Effects of interfacial residual stress on mechanical behavior of SiCf/SiC composites

Study on toughening mechanisms of pyrolytic carbon interface layer in Cf/ZrB2-SiC composites using in-situ tensile experimental and numerical methods

PyC interphase growth mechanism and control models of C/SiC composites

Influences of the dip-coated BN interface on mechanical behavior of PIP-SiC/SiC minicomposites

Effects of Interphase Thickness on Damping Behavior of 2D C/SiC Composites

Preparation and tensile behavior of SiCf/SiC mini composites containing different types and thicknesses of interphase

Residual stress and interface debonding behavior in Si3N4w reinforced SiCN composites prepared by the PIP process: A case study