Abstract:In this study, SiC/SiCN composites with BN interphase were prepared using chemical vapor infiltration (CVI) and polymer infiltration and pyrolysis (PIP) methods. The evolution and related mechanisms of mechanical and microwave absorption properties of the composites after oxidation at 800 degrees C, 1000 degrees C, 1200 degrees C, and 1400 degrees C were investigated. The results showed that with the elevating of oxidation temperature, the flexural strength of SiC/SiCN composites gradually decreased, with a retention rate of 56.7 % after oxidation at 1400 degrees C. The main reasons for the deterioration of mechanical properties were the changes in the crystal structure of SiC fibers under high-temperature conditions and the formation of brittle SiO2 phases on the surface and interior of the SiCN matrix. With the increase in oxidation temperature, the microwave absorption performance of the composites showed an enhancing trend. The main reasons were that after oxidation treatment, the reduction of free carbon content and the formation of SiO2 film layers from the oxidation of SiC and SiCN led to a decrease in the complex permittivity of the composites, resulting in better impedance matching and dielectric loss capabilities. The contributions of BN interphase to stress dispersion, interface polarization, and oxidation protection significantly enhance the mechanical and electromagnetic absorption properties of the composites. Therefore, SiC/ SiCN composites are high-temperature structural microwave absorbing materials with great application prospects.

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Oxidation Behavior of SiBC Matrix Modified C/SiC Composites with Different PyC Interphase Thicknesses

Oxidation Behavior Of A 2d-Sicf/Bn/Sibcn Composite At 1350-1650 Degrees C In Air

Evolution of High Temperature Oxidation Properties of SiCf/SiCN Composites with BN Interphase

Wet oxidation behavior of C/SiC–SiHf(B)CN composites at high temperature

The Oxidation Behaviors of C/SiC Composites Prepared by Precursor Infiltration Pyrolysis Process

Mechanical Properties Evolution of SiCf/SiC Composites with a BN/SiC Multilayer Interface Oxidized at Elevated Temperature

Oxidation Behavior of C/SiC-SiBCN Composites at High Temperature

Oxidation Behavior of C/SiC-Ti3SiC2 at 800–1300 °C in Air

Oxidation Resistance of SiC/SiC Composites Containing SiBC Matrix Fabricated by Liquid Silicon Infiltration

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Long-term Oxidation Behavior of C/SiC-SiBCN Composites in Wet Oxygen Environment

Effects of pyrolysis temperatures on the oxidation behavior of PIP-processed SiCf/SiC composites

Oxidation behaviour of three-dimensional woven C/SiC composites

Microstructural evolution and oxide layer structure of Csf/SiBCN composites during oxidation at 1500 °C

Oxidation Behavior of Tyranno ZMI-SiC Fiber/SiC-SiBC Matrix Composite from 800 to 1200 °C.

Long-term oxidation behaviors and strength retention properties of self-healing SiCf/SiC-SiBCN composites

Degradation mechanisms of a self-healing SiC (f) /BN (i) /[SiC-B 4 C] (m) composite at high temperature under different oxidizing atmospheres

Oxidation behavior of C–SiC composites with a Si–W coating from room temperature to 1500°C

Oxidation resistance of SiCf/SiC composites with a PyC/SiC multilayer interface at 500 °C to 1100°C

Oxidation behavior of oxidation protective coatings for C/C-SiC composites at 1500 ℃