Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Oxidation mechanism of Al–Si–SiC composite at elevated temperature

Study on the oxidation mechanism of Al-SiC composite at elevated temperature

Oxidation behavior of SiC‐AlN ceramics exposed to dry oxygen and water oxygen environments at 1100–1300°C

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Investigation of the oxidation mechanism of Si-Al2O3-fused mullite containing Ti2O3 composite

Formation mechanism of Al4SiC4 in Al–SiC composite under flowing nitrogen at 1300 °C

The interfacial characterization of oxidized SiC(p)/2014 Al composites

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

The oxidation resistance mechanism of SiC-B4C-xAl2O3 ceramics at 1400 °C in air atmosphere

Isothermal Oxidation of Zr2[Al(Si)]4C5–SiC Composites at 1000–1300°C in Air

Phase evolution mechanism of SiC-Al-Si composite under flowing nitrogen at 1600 °C

The Oxidation Resistance Mechanism of SiC-B4C-xAl2O3 Ceramics at 1400 ℃ in Air Atmosphere

Oxidation Resistance of Zr2(Al(Si))4C5-based Composites at Ultra-High Temperature

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

In situ formation mechanism of aluminum oxycarbonitride in the unoxidized zone of Al–Al2O3 composites

Oxidation behavior in wet oxygen environment of Al2O3 added reaction-sintered Si-B-C ceramics

High-temperature Oxidation Behavior of Monolithic Zr3[Al(Si)]4C6 and Its Composite Incorporating 30vol% ZrB2-SiC: Providing a Basis for Broadening the Service Temperature

Oxidation Behaviour of C–SiC–ZrC Composite

Initial damage behavior of Al2O3‐modified SiCf/SiC–B4C composites after oxidation under wet atmosphere at 1200°C

Enhanced mechanical properties of R–SiC honeycomb ceramics with in situ AlN–SiC solid solution

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C