In situ formation mechanism of aluminum oxycarbonitride in the unoxidized zone of Al–Al2O3 composites

Mengyao Yang,Guoqing Xiao,Donghai Ding,Yifan Yang,Mingxue Jiang,Dingao Yang,Shouqian Yuan

DOI: https://doi.org/10.1016/j.ceramint.2021.05.008

IF: 5.532

2021-08-01

Ceramics International

Abstract:The Al–Al2O3 composites were prepared by fused alumina, α-Al2O3 micropowders, and metal aluminum powder. The samples with 3% carbon black (N330), 3% resin powder and α-Al2O3 micropowder, 10% α-Al2O3 micropowder were named S1, S2, and S3, respectively. They were oxidized at 1500 °C for 3 h in a box-type electric furnace, and then the unoxidized areas were analyzed by X-ray diffraction and scanning electron microscopy. It was found that the aluminum oxycarbonitride formed in situ during the oxidation resistance test inhibited further oxidation of S2. The in situ formation mechanism of aluminum oxycarbonitride in the unoxidized zone is believed to be 7Al + 3Al3C4 + 12AlN + 4Al2O3 = 12Al3CON, which is also verified and proven by XRD, SEM and EDS in this work. The oxidation depth of S2 is 46.7% lower than that of S3. Sample S2 hardly has any linear change after fired at 1500 °C × 3 h in coke, which benefits to improve the volume stability and prolongs the service life. Among the three batches, S2 exhibits the minimum creep rate, from 0% to 0.026% at 1500 °C, and the HMOR at 1500 °C in a N2 atmosphere of S2 is 58 MPa. The Al–Al2O3 composites combined with resin strengthened by in situ formed aluminum oxycarbonitride give the composites excellent high-temperature strength owing to the fiber-intersected reinforced microstructure of Al3CON crystals at high temperature. In the Al–C–N–O system, it was found that the general formula of aluminum oxycarbonitride is expressed by Al4n+m(C,O,N)3n+m, and the (n, m) values are (0, 3) for Al3CON.

materials science, ceramics

What problem does this paper attempt to address?

The paper primarily focuses on the oxidation resistance and mechanisms of aluminum-alumina (Al–Al2O3) composites at high temperatures. Specifically:

1. **Research Background and Objectives**:
- Aluminum-based oxide functional ceramics (such as Al2O3) have good resistance to neutral slag corrosion but perform poorly in terms of thermal shock and slag penetration, limiting their application and development.
- By combining oxides and non-oxides (NOCs), the performance of the materials can be improved. Aluminum oxynitride (Al3CON), as a new type of non-oxide material, exhibits excellent performance at high temperatures and can be prepared at lower temperatures.

2. **Main Innovations**:
- Proposed the in-situ formation mechanism of aluminum oxynitride in Al–Al2O3 composites when held at 1500°C for 3 hours: 7Al + 3Al3C4 + 12AlN + 4Al2O3 = 12Al3CON.
- Verified the above mechanism through X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS).
- The oxidation depth of sample S2 was reduced by 46.7% compared to sample S3, with no significant linear change, which helps improve the volume stability and service life of functional ceramics (such as sliding nozzles and sliding gates).

3. **Experimental Results**:
- Sample S2 exhibited the lowest oxidation depth (2.21 mm), while sample S3 had the highest oxidation depth (3.95 mm).
- At 1500°C, sample S2 had a very low creep rate (about 0.026%), showing excellent high-temperature mechanical properties.
- The residual linear change of sample S2 was 0%, which helps improve the stability of functional ceramics such as sliding nozzles and sliding gates.
- The hot modulus of rupture (HMOR) of sample S2 at 1500°C in a nitrogen atmosphere was 58 MPa, significantly higher than other types of composites.

In summary, the paper confirms through detailed research the in-situ formation mechanism of aluminum oxynitride in Al–Al2O3 composites and its significant enhancement of material properties.