Abstract:Due to the high modulus, high strength, low density, excellent wear resistance and good neutron absorption, the boron carbide (B4C) particle reinforced aluminum (Al) matrix composites have been widely applied in the aerospace, weaponry, transportation and neutron shielding fields. In response to the increasing requirement of better strength -ductility matching of B4C/Al composites, introducing a nano-scale reinforcement into the B4C/Al composites becomes an attractive research focus. In this work, the SiC nanowires were ball-milled with Al powders, and then the SiC/Al composite powders were mixed with B4C microparticles. Thus, the 15vol. % B4C/SiC/Al composites with different volume fractions of SiC nanowires were fabricated by hot-pressing sintering and hot extrusion. B4C microparticles and SiC nanowires are uniformly dispersed in the B4C/SiC/Al composites, while the introduced SiC nanowires effectively decrease the Al matrix grain sizes. B4C/SiC/Al composites produce the better strength-ductility matching than that of B4C/Al composites, while the 15vol. % B4C/SiC/Al composite with 1vol. % SiC nanowires achieved the best strength-ductility matching. It generates the 281.7 ± 2.7 MPa in yield strength, 351.2 ± 0.1 MPa in ultimate tensile strength and 5.9 ± 0.7% in failure elongation, which are increased by 18.2%, 15.1% and 13.5% compared to the B4C/Al composites. Uniformly dispersed B4C microparticles and SiC nanowires largely block the dislocation motions and improve the dislocation storage capacity, which results in a more significant hetero-deformation induced (HDI) hardening effect in the B4C/SiC/Al composites. Moreover, the B4C/Al interfacial transition regions with the added SiC nanowires becomes stronger, which can enhance the load transfer efficiency of the B4C/Al interfaces as a result of the existing dislocation hardening zones. In conclusion, it is a good strategy to combine the synergistic strengthening effect of micro-scale and nano-scale reinforcements in the metal matrix composites.

Synthesis and properties of MoAlB composites reinforced with SiC particles

Formation and Oxidation Behavior of Mo-Si-B Composite Coatings with B-rich Interlayer Prepared by Slurry Sintering Method

Preparation, microstructure and mechanical properties of MoAlB-0.15% Si ceramics with superior strength and toughness

The Effect of MoAlB Substitutions on the Oxidation Behavior of ZrB2-SiC Composites at 1600°C

Microstructures and performances of pressureless sintered MoSi2-Al2O3 composites

Fabrication, microstructure characterization and mechanical properties of B4C microparticles and SiC nanowires hybrid reinforced aluminum matrix composites

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Influence of TiC contents on the microstructure, mechanical properties, and oxidation behavior of Mo–10Si–8B alloys

Study on the oxidation mechanism of Al-SiC composite at elevated temperature

Preparation and enhanced oxidation behavior of microalloyed Mo5SiB2 alloy at 1300 °C

High temperature tribological behavior of Mo–12Si–8.5B alloy reinforced with MoAlB ceramic

Preparation of fine-grained MoAlB with preferable mechanical properties and oxidation resistance

Initial damage behavior of Al2O3‐modified SiCf/SiC–B4C composites after oxidation under wet atmosphere at 1200°C

In Situ Synthesis, Mechanical Properties, and Oxidation Resistance of (sic+zrb2)/zr3[al(si)]4c6 Composites

Microstructure, mechanical and friction-wear properties of SiC-WC composite with Al and C as sintering aids

In–situ synthesis of an Al composite reinforced with multi–scale Al12Mo, (Al, Zr, Si) and Al2O3 particles through a multi–stage reaction

Oxidation Behavior of the Si-B-X (X = Mo, Cr, or Ti) Alloys in the Temperature Range of 1000–1400 °C

Synthesis, Microstructure and Mechanical Properties of a MoAlB Ceramic Prepared by Spark Plasma Sintering from Elemental Powders

Effect of Al2O3 addition on the microstructure and oxidation behavior of SiC coating prepared by pack cementation on C/C composites

Microstructure characterization and mechanical properties of in situ synthesized Ti2(Al,Si)C reinforced Al composites

Effect of WSi2 content on oxidation behavior of MoSi2-20 vol% Al2O3 composites