Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

In Situ Synthesis, Mechanical Properties, and Oxidation Resistance of (sic+zrb2)/zr3[al(si)]4c6 Composites

Microstructure, Mechanical, and Thermal Properties of in Situ-Synthesized (zrb2+sic)/zr2[al(si)]4c5 Composites

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Isothermal Oxidation of Zr2[Al(Si)]4C5–SiC Composites at 1000–1300°C in Air

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Effect of boronizing treatment on the oxidation resistance of Zr2(AlSi)4C5/SiC composite

Effect of Lu2O3 addition on the oxidation behavior of SiC-ZrB2 composite coating at 1500 °C: Experimental and theoretical study

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Effect of preset interfacial ZrB 2 particles on the microstructure and properties of C/C-AlSi composites

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Synthesis and properties of MoAlB composites reinforced with SiC particles

Effect of the Y2O3 amount on the oxidation behavior of ZrB2-SiC-based coatings for carbon/carbon composites

Effect of difference in microstructure of rare refractory metal silicate doping matrix on oxidation behavior and mechanism of C/SiC composites

Oxidation Behavior of Sic Platelet-Reinforced Zrb2 Ceramic Matrix Composites

Preparation And Mechanical Properties Of Zirconium Diboride Matrix Composites Reinforced By Silicon Carbon Platelets

Mechanical and Wear Behavior of Al-Si5Cu3/ZrB2 In-Situ Reinforced Metal Matrix Composite

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

Phase stability, hardness and oxidation behaviour of spark plasma sintered ZrB2-SiC-Si3N4 composites

Temperature‐dependent mechanical and oxidation behavior of in‐situ formed ZrN/ZrO2‐containing Si3N4‐based composite

Effect of Si element on improving the oxidation resistance of hybrid (Ti5Si3 + TiC) particles reinforced Ti6Al4V matrix composites

ZrB2 particles reinforced glass coating for oxidation protection of carbon/carbon composites