A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

Lei Zhou,Qiangang Fu,Dou Hu,Jiaping Zhang,Yalong Wei,Jian Zhu,Jingyuan Song,Mingde Tong
DOI: https://doi.org/10.1016/j.corsci.2021.109331
IF: 7.72
2021-05-01
Corrosion Science
Abstract:<p>A dense double layer ZrB<sub>2</sub>-SiC-Si/SiC-Si coating with high content of ZrB<sub>2</sub> was designed and fabricated by dipping-carbonization joint gaseous silicon infiltration. This coating can protect C/C substrate from oxidation in air at 1773 K for 500 h with a weight gain of 1.14%. Such good oxidation protective performance was ascribed to the dense compound silicate oxide layer accompanied by ZrSiO<sub>4</sub>/ZrO<sub>2</sub> pinning phases and compressive stress field around ZrB<sub>2</sub> particles during oxidation. Besides, introducing abundant ZrB<sub>2</sub> phase could inhibit the evaporation of silicate glass at 1973 K, which could protect C/C composites for 78 h with a weight loss of 1.16%.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the easy oxidation of carbon/carbon composites (C/C composites) in high - temperature environments. Specifically, C/C composites have ideal application prospects in the aviation and aerospace fields due to their high strength, high modulus, low density and ultra - high - temperature stability. However, when the temperature exceeds 723 K, these materials will be affected by oxidation in an oxygen - containing environment, which limits their practical application as thermal - structural materials. To overcome this problem, researchers have tried a variety of strategies, one of which is to use ceramic coatings to isolate oxygen to prevent the oxidation of C/C composites. This article focuses in particular on the development of a double - layer ZrB2 - SiC - Si/SiC - Si (ZSS/SS) dense coating with a high content of ZrB2, which is prepared by the combined impregnation - carbonization and vapor - phase silicon infiltration techniques, aiming to improve the antioxidant properties of C/C composites at 1773 K and 1973 K. Studies have shown that this coating can protect the C/C substrate from oxidation for up to 500 hours at 1773 K, with a weight gain of only 1.14%; it can also provide a certain protective effect at 1973 K, with a weight loss of 1.16% after 78 hours. These performance improvements are mainly attributed to the dense composite silicate oxide layer formed in the coating, as well as the role of the ZrSiO_4/ZrO_2 pinning phase and the compressive stress field around the ZrB2 particles. In addition, the introduction of a rich ZrB2 phase can inhibit the evaporation of silicate glass at 1973 K, thereby further protecting the C/C composites.